CA1329167C - Dry etching of silicon carbide - Google Patents
Dry etching of silicon carbideInfo
- Publication number
- CA1329167C CA1329167C CA000581299A CA581299A CA1329167C CA 1329167 C CA1329167 C CA 1329167C CA 000581299 A CA000581299 A CA 000581299A CA 581299 A CA581299 A CA 581299A CA 1329167 C CA1329167 C CA 1329167C
- Authority
- CA
- Canada
- Prior art keywords
- silicon carbide
- plasma
- target
- positioning
- introducing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
DRY ETCHING OF SILICON CARBIDE
Abstract of the Invention The invention comprises a method of etching silicon carbide targets. In one embodiment, a reactive ion plasma is formed from a gas which is easily dissociated into its elemental species in the plasma, for which all of the dissociated elemental species are volatile in the plasma, and for which at least one of the elemental species is reactive with silicon carbide. The silicon carbide target to be etched is positioned on one of the electrodes which is formed from a material with a low sputter yield and which material reacts with a dissociated species to thereby prevent contamination of the target with either sputtered materials from the electrode or polymerized species from the plasma.
Abstract of the Invention The invention comprises a method of etching silicon carbide targets. In one embodiment, a reactive ion plasma is formed from a gas which is easily dissociated into its elemental species in the plasma, for which all of the dissociated elemental species are volatile in the plasma, and for which at least one of the elemental species is reactive with silicon carbide. The silicon carbide target to be etched is positioned on one of the electrodes which is formed from a material with a low sputter yield and which material reacts with a dissociated species to thereby prevent contamination of the target with either sputtered materials from the electrode or polymerized species from the plasma.
Description
S ~ ' ! ~ t-- I
DRY ETCHING OF SILICON CARBIDE
Field of the Invention The present invention generally relates to dry etching methods for making electronic devices such as semiconductor devices or the like, and especially to a dry etching technique for etching silicon carbide (SiC).
Background of the Invention In the manufacture of electronic devices ,~ from semiaonductor materials, one technique of interest is the selective building up, followed by the selective removal, o~ various layers of different materials, so that the building up and removal processes result in specific electronic devices such as transistors, diodes, capacitors and the like~ :
One technique for removing layers of semiconductor or other materials from a given substrate is known as etching, which is the removal of a material following its interaction with another material generally referred to as the etchant.
Etching techniques fall into two broad categories:
wet etching which generally refers to tPchniques . which take place in solutions or molten salts or other liquid materials; and dry etching which ~5 generally refers to the use of gases or plasmas to , perform the removal which is desired.
7 Dry etching techniques are of particular ~, interest in producing electronic devices because they generally exhibit better resolution and !
, ,, ,: . , .
~ 1 32~ 1 ~7 .. . .
,~ ~
improved dimensional and shape control capabilities than do the various methods of wet etching.
Accordingly, dry etching is favorably utili~ed where superior pattern control and delineation is required such as the processing of semiconductor wafers to form large scale integrated devices and integrated circuits.
Dry etching techniques can be used to micromachine mesas, isolation trenches, backside s 10 contact via holes, and other forms of pattern definition on thin ~ilms, substrates, or other material~. -One perennial candidate material for use in semiconductor devices--and which correspondingly requires etching in order to form certain of these devices--is silicon carbide (SiC). Silicon carbide has long heen recognized as having certain favorable characteristics as a semiconductor material, including its wide bandgap, high thermal l 20 conductivity, high saturated electron drift i velocity, and high electron mobility. To date, however, silicon carbide has not reached the commercial position in the manufacture of electronic devices that would be expected on the basis of its excellent semiconductor properties. This is a result of the difficulties encountered in working with silicon carbide: high process temperatures are Z often required~ good starting materials can be difficult to obtain, certain doping techniques have 30 heretofore been difficult to accomplish, and~perhaps most importantly, silicon carbide crystallizes in over 150 polytypes, many of which are separated by ` very small thermodynamic differences. Accordingly, controlling the growth of single crystals or 35 monocrystalline thin films of silicon carbide which are of a sufficient quality to make electronic , .
, .
~ ~ ~ 3 ~ 1 3291 ~7 ;~ devices practical and useful, has eluded researchers.
Recently, however, a number of developments have been accomplished which offer the ability to grow large `~ single crystals of device quality silicon carbide, thin films of device quality silicon carbide, and to introduce dopants into silicon carbide, as requixed in the manufacture of many eIectronic devices. These developments are the subject of co-pending patent applications which have been assigned to the common ~ 10 assignee of the present invention and which may be ,!. referenced as circumstances dictate~ These include:
` "Growth of Beta-SiC Thin Films and Semiconduct~or Devices , Fabricated Thereon", Cdn. Serial No. 581,147, filed I October 25, 1988 (see U.S. Patent 4,912,063, March 27, 1990); "Homoepitaxial Growth of Alpha-SiC Thin Films and Semiconductor Devices Fabricated Thereon", Cdn. Serial No.
581,144, filed October 25, 1988 (see U.S. Patent ` 4,912,064, March 27, 1990); "Sublimation of Silicon ~, Carbide to Produce Large Device Quality Single Crystals of Silicon Carbide", Cdn. Serial No. 581,145, filed October 25, 1988 (see U.S. Patent 4,886,005, September 12, 1989);
and "Implantation and Electrical Activation of Dopants ; into Mono-crystalline Silicon Carbide", Cdn. Serial No.
~ 581,148, filed October 25, 1988.
-` 25 With the successes offered by these developments, ` an appropriate technique for etching silicon carbide is `' likewise desirable, for example in the production of mesa-; type structures or any other structures in which etching ~' is required.
A number of investigators have attempted-to develop methods for etching silicon carbide under circumstances in which silicon carbide is used as a mask for a patterning process rather than as the active semiconductor portion of , an electronic device. An early U.S. patent to Haga, No.
~, 35 3,398,033, discusses a method of etching silicon carbide using a mixture of oxygen and chlorine ~T .
~, ;,~,:, ," ,, .
. . !
:
''~ ' " .~ \~, '. ' ', . ' , .
; heated to between 1200 and 1300C. According to ; Haga, this process partially deteriorates the silicon carbide, after which th~ remainder can be removed by a wet reaction in a mixture of hydrofluoric and nitric acids.
Yonezawa, U.S. Patent No. 4,351,894, also discusses the use of silicon carbide as a mask material in manufacturing electronic devices from other semiconductor materials. According to Yonezawa, removal of silicon carbide is accomplished by either a plasma etching process using carbon tetrafluoride and oxygen, or by an electrolytic etching technique in which an electrolyte is selected from a mixture of perchloric acid, acetic acid and water; or from formic acid; or a mixture of sulfuric acid and water.
In a later patent, U.S. No. 4,560,642, Yonezawa discusses a slightly different kechnique for using silicon carbide as a mask material, but describes Z0 identical etching processes for removing the silicon carbide mask.
Yamazaki~ U.S. Patent No. 4,595,453, discusses a method of forming a semiconductor substrate, rather than a mask, which may be formed of silicon carbide. Yamazaki suggests using hydrogen fluoride gas tHF) as the reactive gas plasma for selectively or nonselectively etching the semiconductor silicon carbide substrate.
In the scientific literature, Lu et al., ~ 30 Thermal Oxidation of Sputtered Silicon Carbide Thin '~ Films, J. Electrochem. Soc., 131, 1907 (1984), discuss masking techniques using amorphous silicon carbide films, and using mixtures of tetrafluoramethane (CF4) and oxygen, as well as nitrogen trifluoride ~NF3) as mask-removing reactive ion etching plasmas. The thin films described by Lu, however, are sputter deposited films of silicon ... , :-.
., .
. . . ~ : ` , -~
., .
1 32q 1 67 ~ -5-s carbide, a technique which results in either amorphous layers or partially polycrystalline layers which for practical purposes are amorphous. As is known to those familiar with semiconductor materials and their properties, such amorphous or polycrystalline materials are essentially useless for forming the active portion of remiconductor devices. Furthermore, Lu offers only a general ; discussion of the etching he reports carrying out.
By way of background, reactive ion etching is a procedure in which the material to be etched, sometimes called the target, is placed on a cathode in an electric field, and in the presence of a selected vaporized material. A potential is applied across the anode and cathode which is sufficient to ionize atoms and molecules in the vapor, as well as to produce some radicals. The potential difference accelerates positively charged ions in the vapor towards the target on the cakhode. As these ions strike the material, they physically etch it away.
In reactive ion etching, the vaporized material is selected to chemically react with the target material, thus enhancing the effects of the physical collisions.
In producing devices using such dry ~ etching technigues, certain problems occur which `~ must be addressed before successful results can be obtained. For example, when a gas like tetrafluoromethane (CF4) is used as the reactant gas, i 30 polymerization tends to occur among the fluorocarbon radicals formed, which in turn cause fluorocarbon compounds to deposit onto the surface being etched.
These impurities, however, are undesirable whenever the etched surface is to be used for silicon carbide-based eleckronic devices. Because high quality ohmic contacts must eventually be made on the etched surface in order to produce workable . . .
~ .
1 32~ 1 67 . . .
devices, a smooth, chemically clean etch is imperative.
Accordingly, it is an object of the present invention to provide a method of dry etching monocrystalline silicon carbide which produces a ::`
~`~ smooth and chemically clean etched surface.
~. It is another object of the invention to ',5 provide a method for dry etching of silicon carbide using plasma etching, reactive ion etching, or reactive ion beam etching processes.
It is a further object of the invention to produce faster etch rates than have been possible to date for the dry etching of silicon carbide.
It is another object of the invention to ~ 15 provide a method of dry etching of silicon carbide ;j with nitrogen trifluoride and mixtures of nitrogen ! trifluoride with other gases such as oxygen or ~, argon.
;~ It is a further object of the invention to ~j, 20 provide a method of dry etching silicon carbide by controlling the etchant gas used to form the plasma and the electrodes used in the ionization process.
It is another object of this invention to provide a method of dry etching of silicon carbide , 25 in which the etchant is efficiently broXen into free radicals and for which all of the by-products of ionization are volatile.
It is a further object of this invention to provide a method of reactive ion etching of J, 30 silicon carbide using electrode materials which exhibit low sputter yield and which will react with the by-products of ionization so that they will not ¦ affect the etched surface.
:i:
., r13 :j I B
.
. ~ . . . . . .. .
. . . ; . ~. . -. ....
.~ . . . .. ~ ` . .; ;. ~ ..
- The invention in one broad aspect provides a method of etching a silicon carbide target comprising applying a plasma generating potential across two electrodes; generating a plasma between the two electrodes by introducing a gas between the electrodes, and wherein the gas is easily dissociated substantially into its elemental species in the plasma and wherein substantially all of the dissociated species from the gas are volatile in the plasma and wherein at least one of the dissociated species is reactive with silicon carbide;
and positioning a silicon carbide target to be etched on one of the electrodes, and wherein the electrode is formed from a material with a low sputter yield and wherein the electrode material is reactive with the ~ 15 dissociated species; and reacting the plasma with the ; silicon carbide to thereby etch the silicon carbide, wherein the reaction of the dissociated species with the electrode, and the electrode's low sputter yield, prevent ` contamination of the target with either sputtered i 20 materials from the supporting electrode or unreacted dissociated species from the plasma.
The invention in another broad aspect provides a method of etching of a silicon carbide target comprising applying a plasma generating potential across an anode and a carbon cathode; generating a plasma between the anode and the carbon cathode by introducing nitrogen trifluoride therebetween; positioning a silicon carbide target to be etched on the carbon cathode whereby the carbon cathode exhibits a low sputter yield and is reactive with dissociated fluorine from the nitrogen trifluoride; and reacting the plasma with the silicon carbide to thereby etch the silicon carbide, wherein the reaction of dissociated fluorine with the carbon cathode, ` and the cathode's low sputter yield, prevent contamination of the target with either sputtered carbon materials from the cathode or polymerized fluorine .species from the plasma.
, ~
, ~
,' ' ~ ' : . :
" . ~
.
1 32~ 1 67 .:
~The foregoing objects, aspects and advantages and ;~. other features of the invention will be set forth in the accompanying detailed description, in which preferred and .
,exemplary embodiments are set forth, . .
~'', : ,.
;, ., :., ., .
, .~
c 1;
:"1 ~, , .
, ' !
:j ~, `.~
"
.j :
,' ~:1 ~, `, `';
`" ~3 ' ` . : .~ ' : , , ' , `
`~
` _7_ 1 329 1 67 taken in conjunction with the accompanying drawings in which:
escription of the Drawinqs ~ Figure 1 shows two Auger slectron spectra .~ 5 obtained for an unetched silicon carbide surface and ~`: a silicon carbide surface after reactive ion etching :~ in carbon tetrafluoride using a stainless steel `- cathode;
Figure 2 is an electron micrograph of a lo silicon carbide surface after reactive ion etching ~ in carbon tetrafluoride using a stainless steel i cathode:
Figure 3 is an electron micrograph of an : etched surface of silicon carbide following a reactive ion etching in carbon tetrafluoride using anodized aluminum cathode;
Figure 4 illustrates two Auger electron : spectra of an etched surface of silicon carbide following (a) reactive ion etching in carbon tetrafluoride, and (b) reactive ion etch.ing in NF3, both using an anodized aluminum cathodç;
~ Figure 5 is an electron micrograph of an : etched surface of silicon carbide after reactive ion etching in NF3 using an anodized aluminum cathode;
Figure 6 illustrates two Auger electron spectra for a sample of silicon carbide etched with . (a) CF4, and (b) NF3, both using a carbon cathode;
`. Figure 7 is an electron micrograph of an ~;, etched surface of silicon carbide following reactive ion etching in carbon tetrafluoride, using a~carbon ,``~ cathode;
Figure 8 is an electron micrograph of an ~ etched surface of silicon carbide following reactive :d, ion etching in NF3 using a carbon cathode; and ;~ 35 Figure 9 is another electron micrograph of an etched surface of silicon carbide following reactive ion etching in NF3 using a carbon cathode.
, ;
A
., ~ .
-~, -8- 1 32q 1 67 Summary of the Invention The invention comprises a method of etching monocrystalline thin films and single crystals o~ silicon carbide using nitrogen `~ 5 trifluoride (NF3). Following etching, the etched surfaces were characterized by Auger electron spectroscopy (AES) and scanning electron microscopy (SEM). By using a carbon cathode, a very smooth and - much cleaner surface resulted than was obtained using other cathodes. In comparison to other techni~ues, the optimal conditions for etching silicon carbide are using NF3 and a carbon cathode.
` Detailed Description The present invention comprises a method of dry etching of silicon carbide using NF3 as the etchant. In this technique, the NF3 gas is dissociated in a plasma and the dissociated species (radicals) etch the silicon carbide which is ; immersed in the plasma. As is known to those familiar with plasma physics, there is a synergistic ef~ect between the radicals and the ions in the plasma that allow very inert materials to be etched.
The radicals and ions that result from the plasma can be introduced to the silicon carbide in one o~
three different ways; plasma etching, reactive ion etching, and reactive ion beam etching. In plasma etching, no direct current bias is applied other than the field required to generate the plasma. In reactive ion etching ~RIE), a direct current bias is applied to the system in addition to the plasma-generating field and induces directional ion bombardment. Where desired, a magnet can be positioned behind the target to enhance the RIE
process, a technique known as magnetron etching. In reactive ion beam etching, the ions are directed from a source chamber to a negatively biased silicon carbide target, which is also often maintained in a , .
, . ~, .
.:
~ ' ' ' ', ' ' . ', ,` ' ` . ' ' " , . . .
--"` t 32q 1 67 g carbide target, which is also often maintained in a higher vacuum (lesser pressure~ target chamber. The NF3 can be ionized in either a radio freguency (r~), ~; microwave, direct current (DC) or electron cyclotron J'. 5 resonance (ECR) plasma, depending upon the desired c process.
Silicon carbide is chemically very inert and can only be conventionally etched by molten salts, or by chlorine or hydrogen gases at high ~ 10 temperatures. The dry etching techniques of the- present invention offer a more controllable low-temperature method of etching silicon carbide.
; As further stated above, however, previous attempts have shown that dry-etching silicon carbide using more conventional gases such as CF4 leaves a graphitic surface contaminated with materials such as fluorocarbon polymers. These surface conditions , are undesirable where the etched surface is being -~ prepared for making ohmic contacts for an electronic device.
~ Therefore, a desirable gas for etching ;~;1 silicon carbide should be readily dissociable into etching radicals and not into non-etching radicals, ~ ions or molecules which merely contaminate the `~ 25 target. Nitrogen trifluoride is one such desirable gas because it can be efficiently broken into ,J' nitrogen and free fluorine radicals, and because all i~ of the possible by-products of the ionization .~
process are volatile. As a result, surfaces etched with NF3 tend to be very clean. Where desired, the A~ NF3 can be mixed with other gases~ particularlyoxygen (2~ and argon (Ar~ in the method of the ; present invention.
`3: In particular embodiments of the present invention, thin films of beta silicon carbide which had been epitaxially grown on silicon (100) substrates were etched. As indicated in the J
.~~
''' ' ~ ' .", ' ' :~.
.
, . . : ~ .
, . . .
co-pending applications incorporated by reference, however, it is now possible to successfull~ grow device quality silicon carbide thin films upon -~ silicon carbide substrates and the etching techniques of the present inventio,n are equally applicable under these circumstancles.
Following the growth of the beta silicon ~` carbide thin films, the samples were polished with diamond paste, oxidized, etched in hydrofluoric acid, and rinsed in deionized water. The samples that were analyzed using scanning electron microscopy (SEM) were masked with evaporated aluminum that was patterned using standard photolithographic techniques. The samples used ~or Augex electron spectroscopy (AES) were left unmasked.
In a particular embodiment of the invention, the reactive ion etching techniques were performed in a parallel plate reactor with a 28.0 cm diameter aluminum anode, a 17.0 cm diameter anodized aluminum cathode, and a plate separation o~ 5.0 cm.
The samples were placed directly on the anodized aluminum cathode or, as discussed more ~ully herein, on a carbon cover plate over the anode. The samples were kept at temperatures of 308K. A 13.56 megahertz (MHz) rf supply powered the cathode at densities of 0.440 to 0.~48 watts per square centimeter (W/cm2). The chamber was evacuated to a pressure of 5 X 10-5 Torr and the NF3 was introduced at 25 standard cubic centimeters per minute (sccm) while the pressure was maintained at 40 millitorr ' (4x10-2 torr~. In general, flow rates of from about i 1 to about 500 sccm are appropriate with about 20 to about 60 sccm preferred. It should be understood that nitrogen trifluoride gas is an extremely toxic material and must be handled carefully and under the proper precautions in carrying out the techniques of the present invention.
As is known to those familiar with plasma science, a plasma can be formed uncler a number of gas pre~sure and electric power conditions. For example, natural lightning is a plzlsma effect which takes place at atmospheric pressure under the application of enormous amounts of electric power.
For scientific and commercial purposes, however, normally available power supplies make plasma formation much more feasible at lower gas pressures.
At moderate power supply l~vels (typically between about 10 and about 400 Watts to the powered electrode) a gas pressure of between about 5 and about 60 milliTorr (mTorr, i.e. between about 5x10-3 and 60x10-3 mTorr) are appropriately used, although in some cases, pressures high as 10 Torr are still appropriate. Using typical eguipment, this results in power densities of between about 0.04 and about 2 watts per square centimeter (W/cm2), with densities of between about 0.4 and about 0.9 W/cm2 preferred.
At generally lower pressures, the amount of gas present is insufficient to support the number of collisions required to maintain the plasma. At generally higher pressures, so much gas is present that the increased number of collisions tends to first dampen, and then quench, the plasma. It should be understood, therefore, that the selection of temperatures, power levels, and gas pressures used in practicing the present invention can vary widely and t~at those specified herein are given by way of example, and not as limitations on the scope of the invention.
Auger electron spectroscopy was used to analyze both the starting materials and the etched surfaces. Figure l(a) shows a typical AES spectrum for unetched beta silicon carbide, and indicates the .: , , ,~
". ~
.: :
.
~ i 1329167 presence of silicon, carbon, and oxygPn, present as a native oxide.
As stated earlier, a polymerization problem is commonly associated when halogenated hydrocarbons such as CF4 are used as the etchant.
This is illustrated by the AES spectra o~ Figures ~-~ 4(a~ and ~(b) which show a ~ignificant presence of ~' fluorine (~) on the etched surfaces. It has been discovered according to the present invention, however, that fluorine is the chief reactant for both silicon and carbon. ~his reaction scheme makes NF3 a desirable gas for etching SiC because it is moxe efficiently broken into free F radicals than are fluorinated hydrocarbons, and secondly because all of the possible by-products of its ionization ; are volatile. The practical advantages of these theoretical advantages were observed in the present invention in which etch rates were observed as fast .~i as 211 nanometers per minute (nm/min), which are the ` 20 highest etch rates ever reported for the dry etching :
of silicon carbide using any technique.
`:;
In the particular embodiment represented by Figures 3, 4 and 5, the reactive ion etching was carried out using an anodized aluminum cathode to ~` 25 support the SiC target. Under these conditions, ! however, there existed an apparent presence of some ~ aluminum oxide (A1203) on the etched surface, as ; demonstrated by the Auger electron spectrum of Figure 4(b). Additionally, the somewhat rough surface shown in the micrograph of Figure 5 ~as ~` observed foilowing the N~3 etching using the anodized aluminum cathode. Although applicant does not wish to be bound by any particular theory, it is believed ~;l that this results from Al203 which has sputtered from the cathode and masked small portions of the surface, a process referred to as nmicromasking."
The presence of iron (Fe) in the AES spectrum of ~' , i. .
,,, , :
: . .
; - 1329167 Figure l~b) and the rough surface seen in the micrograph of Figure 2 demonstrate the occurence of this same effect when a stainless steel cathode was used to support the target.
The presence of fluorine on the etched ; surface is also demonstrated by the AES spectrum in Figure 4~b). Presently, it is believed that the lack of reactivity between the anodized aluminum cathode and the fluorins species allows the fluorine ~i 10 species to undesirably accumulate and polymerize on the etched surfacs.
1.
Therefore, in order to eliminate the r. surface deposition of both fluorine and Al203, in a preferred embodiment of the invention a carbon cathode cover plate was placed in the RIE chamber.
Carbon has several advantages in the method of the present invention: it has a very low sputter yield, and it is reactive with fluorine. As is known to those familiar with these technologies, sputtering occurs when an ion strikes a surface knocking an atom, molecule or ion loose from that surface as a result of the energy imparted by the impinging ion.
1 This sputtered particle can be ejected from the cathode and deposit on the sur~ace being etched, leading to the undesired impurity or micromasking referred to earlier herPin. Of course, under certain circumstances, sputtering is a desired technique for depositing a particular material upon another material.
When the carbon cathode cover plate was used for the reactive ion etching of silicon carbide `~! in pure NF3, the greatly improved AES spectrum shown in Figure 6~b) resulted. This indicates that the surface is very clean, with no fluorine peak visible and only a minor amount of nitrogen present after etching. As stated above, the carbon in the cathode reacts with the fluorine, keeping the fluorine from i ;~~
.~. . .
, ~ .
~: .
, . ;
. .
,~ , :.: .
1 32q 1 67 accumulating and polymerizing upon the etched silicon carbide surface.
The differences between the use of the carbon cathode cover and the anodized aluminum cathode are demonstrated by Figure 5 (anodized aluminum cathode) and Figures 7, 8 and 9 which shows the smooth, etched surface of silicon carbide after reactive ion etching in CF4 (Figure 7) and in nitrogen trifluoride (Figures 8 and ~) using the carbon cathode.
Additionally, in spite of the use of carbon cathode in this embodiment, Figure 6(b) shows no significant increase in the carbon signal of the AES spectrum.
The invention thus demonstrates that in the reactive ion etching of silicon carbide, the choice of cathode material plays a major role in the chemical and physical characteristics of the etched surface. Because high quality ohmic contacts require both a smooth and a chemically clean surface, the invention provides an optimal configuration for dry etching of silicon carbide by using nitrogen trifluoride and a carbon cathode.
Given these characteristics, the invention comprises a method of patterning silicon carbide in the formation of electronic devices. By forming an appropriate masked pattern on the silicon carbide, etching it according to the present invention, and then removing the mask, desired patterns and devices can be fabricated.
In the specification, there have been set forth preferred and exemplary embodiments, which have been included by way of example and not limitation, the scope of the invention being set forth in the following claims:
-:: ; , , " .
. :, .
:':' ~ :
~ : . ' , ' ' ' ' .
DRY ETCHING OF SILICON CARBIDE
Field of the Invention The present invention generally relates to dry etching methods for making electronic devices such as semiconductor devices or the like, and especially to a dry etching technique for etching silicon carbide (SiC).
Background of the Invention In the manufacture of electronic devices ,~ from semiaonductor materials, one technique of interest is the selective building up, followed by the selective removal, o~ various layers of different materials, so that the building up and removal processes result in specific electronic devices such as transistors, diodes, capacitors and the like~ :
One technique for removing layers of semiconductor or other materials from a given substrate is known as etching, which is the removal of a material following its interaction with another material generally referred to as the etchant.
Etching techniques fall into two broad categories:
wet etching which generally refers to tPchniques . which take place in solutions or molten salts or other liquid materials; and dry etching which ~5 generally refers to the use of gases or plasmas to , perform the removal which is desired.
7 Dry etching techniques are of particular ~, interest in producing electronic devices because they generally exhibit better resolution and !
, ,, ,: . , .
~ 1 32~ 1 ~7 .. . .
,~ ~
improved dimensional and shape control capabilities than do the various methods of wet etching.
Accordingly, dry etching is favorably utili~ed where superior pattern control and delineation is required such as the processing of semiconductor wafers to form large scale integrated devices and integrated circuits.
Dry etching techniques can be used to micromachine mesas, isolation trenches, backside s 10 contact via holes, and other forms of pattern definition on thin ~ilms, substrates, or other material~. -One perennial candidate material for use in semiconductor devices--and which correspondingly requires etching in order to form certain of these devices--is silicon carbide (SiC). Silicon carbide has long heen recognized as having certain favorable characteristics as a semiconductor material, including its wide bandgap, high thermal l 20 conductivity, high saturated electron drift i velocity, and high electron mobility. To date, however, silicon carbide has not reached the commercial position in the manufacture of electronic devices that would be expected on the basis of its excellent semiconductor properties. This is a result of the difficulties encountered in working with silicon carbide: high process temperatures are Z often required~ good starting materials can be difficult to obtain, certain doping techniques have 30 heretofore been difficult to accomplish, and~perhaps most importantly, silicon carbide crystallizes in over 150 polytypes, many of which are separated by ` very small thermodynamic differences. Accordingly, controlling the growth of single crystals or 35 monocrystalline thin films of silicon carbide which are of a sufficient quality to make electronic , .
, .
~ ~ ~ 3 ~ 1 3291 ~7 ;~ devices practical and useful, has eluded researchers.
Recently, however, a number of developments have been accomplished which offer the ability to grow large `~ single crystals of device quality silicon carbide, thin films of device quality silicon carbide, and to introduce dopants into silicon carbide, as requixed in the manufacture of many eIectronic devices. These developments are the subject of co-pending patent applications which have been assigned to the common ~ 10 assignee of the present invention and which may be ,!. referenced as circumstances dictate~ These include:
` "Growth of Beta-SiC Thin Films and Semiconduct~or Devices , Fabricated Thereon", Cdn. Serial No. 581,147, filed I October 25, 1988 (see U.S. Patent 4,912,063, March 27, 1990); "Homoepitaxial Growth of Alpha-SiC Thin Films and Semiconductor Devices Fabricated Thereon", Cdn. Serial No.
581,144, filed October 25, 1988 (see U.S. Patent ` 4,912,064, March 27, 1990); "Sublimation of Silicon ~, Carbide to Produce Large Device Quality Single Crystals of Silicon Carbide", Cdn. Serial No. 581,145, filed October 25, 1988 (see U.S. Patent 4,886,005, September 12, 1989);
and "Implantation and Electrical Activation of Dopants ; into Mono-crystalline Silicon Carbide", Cdn. Serial No.
~ 581,148, filed October 25, 1988.
-` 25 With the successes offered by these developments, ` an appropriate technique for etching silicon carbide is `' likewise desirable, for example in the production of mesa-; type structures or any other structures in which etching ~' is required.
A number of investigators have attempted-to develop methods for etching silicon carbide under circumstances in which silicon carbide is used as a mask for a patterning process rather than as the active semiconductor portion of , an electronic device. An early U.S. patent to Haga, No.
~, 35 3,398,033, discusses a method of etching silicon carbide using a mixture of oxygen and chlorine ~T .
~, ;,~,:, ," ,, .
. . !
:
''~ ' " .~ \~, '. ' ', . ' , .
; heated to between 1200 and 1300C. According to ; Haga, this process partially deteriorates the silicon carbide, after which th~ remainder can be removed by a wet reaction in a mixture of hydrofluoric and nitric acids.
Yonezawa, U.S. Patent No. 4,351,894, also discusses the use of silicon carbide as a mask material in manufacturing electronic devices from other semiconductor materials. According to Yonezawa, removal of silicon carbide is accomplished by either a plasma etching process using carbon tetrafluoride and oxygen, or by an electrolytic etching technique in which an electrolyte is selected from a mixture of perchloric acid, acetic acid and water; or from formic acid; or a mixture of sulfuric acid and water.
In a later patent, U.S. No. 4,560,642, Yonezawa discusses a slightly different kechnique for using silicon carbide as a mask material, but describes Z0 identical etching processes for removing the silicon carbide mask.
Yamazaki~ U.S. Patent No. 4,595,453, discusses a method of forming a semiconductor substrate, rather than a mask, which may be formed of silicon carbide. Yamazaki suggests using hydrogen fluoride gas tHF) as the reactive gas plasma for selectively or nonselectively etching the semiconductor silicon carbide substrate.
In the scientific literature, Lu et al., ~ 30 Thermal Oxidation of Sputtered Silicon Carbide Thin '~ Films, J. Electrochem. Soc., 131, 1907 (1984), discuss masking techniques using amorphous silicon carbide films, and using mixtures of tetrafluoramethane (CF4) and oxygen, as well as nitrogen trifluoride ~NF3) as mask-removing reactive ion etching plasmas. The thin films described by Lu, however, are sputter deposited films of silicon ... , :-.
., .
. . . ~ : ` , -~
., .
1 32q 1 67 ~ -5-s carbide, a technique which results in either amorphous layers or partially polycrystalline layers which for practical purposes are amorphous. As is known to those familiar with semiconductor materials and their properties, such amorphous or polycrystalline materials are essentially useless for forming the active portion of remiconductor devices. Furthermore, Lu offers only a general ; discussion of the etching he reports carrying out.
By way of background, reactive ion etching is a procedure in which the material to be etched, sometimes called the target, is placed on a cathode in an electric field, and in the presence of a selected vaporized material. A potential is applied across the anode and cathode which is sufficient to ionize atoms and molecules in the vapor, as well as to produce some radicals. The potential difference accelerates positively charged ions in the vapor towards the target on the cakhode. As these ions strike the material, they physically etch it away.
In reactive ion etching, the vaporized material is selected to chemically react with the target material, thus enhancing the effects of the physical collisions.
In producing devices using such dry ~ etching technigues, certain problems occur which `~ must be addressed before successful results can be obtained. For example, when a gas like tetrafluoromethane (CF4) is used as the reactant gas, i 30 polymerization tends to occur among the fluorocarbon radicals formed, which in turn cause fluorocarbon compounds to deposit onto the surface being etched.
These impurities, however, are undesirable whenever the etched surface is to be used for silicon carbide-based eleckronic devices. Because high quality ohmic contacts must eventually be made on the etched surface in order to produce workable . . .
~ .
1 32~ 1 67 . . .
devices, a smooth, chemically clean etch is imperative.
Accordingly, it is an object of the present invention to provide a method of dry etching monocrystalline silicon carbide which produces a ::`
~`~ smooth and chemically clean etched surface.
~. It is another object of the invention to ',5 provide a method for dry etching of silicon carbide using plasma etching, reactive ion etching, or reactive ion beam etching processes.
It is a further object of the invention to produce faster etch rates than have been possible to date for the dry etching of silicon carbide.
It is another object of the invention to ~ 15 provide a method of dry etching of silicon carbide ;j with nitrogen trifluoride and mixtures of nitrogen ! trifluoride with other gases such as oxygen or ~, argon.
;~ It is a further object of the invention to ~j, 20 provide a method of dry etching silicon carbide by controlling the etchant gas used to form the plasma and the electrodes used in the ionization process.
It is another object of this invention to provide a method of dry etching of silicon carbide , 25 in which the etchant is efficiently broXen into free radicals and for which all of the by-products of ionization are volatile.
It is a further object of this invention to provide a method of reactive ion etching of J, 30 silicon carbide using electrode materials which exhibit low sputter yield and which will react with the by-products of ionization so that they will not ¦ affect the etched surface.
:i:
., r13 :j I B
.
. ~ . . . . . .. .
. . . ; . ~. . -. ....
.~ . . . .. ~ ` . .; ;. ~ ..
- The invention in one broad aspect provides a method of etching a silicon carbide target comprising applying a plasma generating potential across two electrodes; generating a plasma between the two electrodes by introducing a gas between the electrodes, and wherein the gas is easily dissociated substantially into its elemental species in the plasma and wherein substantially all of the dissociated species from the gas are volatile in the plasma and wherein at least one of the dissociated species is reactive with silicon carbide;
and positioning a silicon carbide target to be etched on one of the electrodes, and wherein the electrode is formed from a material with a low sputter yield and wherein the electrode material is reactive with the ~ 15 dissociated species; and reacting the plasma with the ; silicon carbide to thereby etch the silicon carbide, wherein the reaction of the dissociated species with the electrode, and the electrode's low sputter yield, prevent ` contamination of the target with either sputtered i 20 materials from the supporting electrode or unreacted dissociated species from the plasma.
The invention in another broad aspect provides a method of etching of a silicon carbide target comprising applying a plasma generating potential across an anode and a carbon cathode; generating a plasma between the anode and the carbon cathode by introducing nitrogen trifluoride therebetween; positioning a silicon carbide target to be etched on the carbon cathode whereby the carbon cathode exhibits a low sputter yield and is reactive with dissociated fluorine from the nitrogen trifluoride; and reacting the plasma with the silicon carbide to thereby etch the silicon carbide, wherein the reaction of dissociated fluorine with the carbon cathode, ` and the cathode's low sputter yield, prevent contamination of the target with either sputtered carbon materials from the cathode or polymerized fluorine .species from the plasma.
, ~
, ~
,' ' ~ ' : . :
" . ~
.
1 32~ 1 67 .:
~The foregoing objects, aspects and advantages and ;~. other features of the invention will be set forth in the accompanying detailed description, in which preferred and .
,exemplary embodiments are set forth, . .
~'', : ,.
;, ., :., ., .
, .~
c 1;
:"1 ~, , .
, ' !
:j ~, `.~
"
.j :
,' ~:1 ~, `, `';
`" ~3 ' ` . : .~ ' : , , ' , `
`~
` _7_ 1 329 1 67 taken in conjunction with the accompanying drawings in which:
escription of the Drawinqs ~ Figure 1 shows two Auger slectron spectra .~ 5 obtained for an unetched silicon carbide surface and ~`: a silicon carbide surface after reactive ion etching :~ in carbon tetrafluoride using a stainless steel `- cathode;
Figure 2 is an electron micrograph of a lo silicon carbide surface after reactive ion etching ~ in carbon tetrafluoride using a stainless steel i cathode:
Figure 3 is an electron micrograph of an : etched surface of silicon carbide following a reactive ion etching in carbon tetrafluoride using anodized aluminum cathode;
Figure 4 illustrates two Auger electron : spectra of an etched surface of silicon carbide following (a) reactive ion etching in carbon tetrafluoride, and (b) reactive ion etch.ing in NF3, both using an anodized aluminum cathodç;
~ Figure 5 is an electron micrograph of an : etched surface of silicon carbide after reactive ion etching in NF3 using an anodized aluminum cathode;
Figure 6 illustrates two Auger electron spectra for a sample of silicon carbide etched with . (a) CF4, and (b) NF3, both using a carbon cathode;
`. Figure 7 is an electron micrograph of an ~;, etched surface of silicon carbide following reactive ion etching in carbon tetrafluoride, using a~carbon ,``~ cathode;
Figure 8 is an electron micrograph of an ~ etched surface of silicon carbide following reactive :d, ion etching in NF3 using a carbon cathode; and ;~ 35 Figure 9 is another electron micrograph of an etched surface of silicon carbide following reactive ion etching in NF3 using a carbon cathode.
, ;
A
., ~ .
-~, -8- 1 32q 1 67 Summary of the Invention The invention comprises a method of etching monocrystalline thin films and single crystals o~ silicon carbide using nitrogen `~ 5 trifluoride (NF3). Following etching, the etched surfaces were characterized by Auger electron spectroscopy (AES) and scanning electron microscopy (SEM). By using a carbon cathode, a very smooth and - much cleaner surface resulted than was obtained using other cathodes. In comparison to other techni~ues, the optimal conditions for etching silicon carbide are using NF3 and a carbon cathode.
` Detailed Description The present invention comprises a method of dry etching of silicon carbide using NF3 as the etchant. In this technique, the NF3 gas is dissociated in a plasma and the dissociated species (radicals) etch the silicon carbide which is ; immersed in the plasma. As is known to those familiar with plasma physics, there is a synergistic ef~ect between the radicals and the ions in the plasma that allow very inert materials to be etched.
The radicals and ions that result from the plasma can be introduced to the silicon carbide in one o~
three different ways; plasma etching, reactive ion etching, and reactive ion beam etching. In plasma etching, no direct current bias is applied other than the field required to generate the plasma. In reactive ion etching ~RIE), a direct current bias is applied to the system in addition to the plasma-generating field and induces directional ion bombardment. Where desired, a magnet can be positioned behind the target to enhance the RIE
process, a technique known as magnetron etching. In reactive ion beam etching, the ions are directed from a source chamber to a negatively biased silicon carbide target, which is also often maintained in a , .
, . ~, .
.:
~ ' ' ' ', ' ' . ', ,` ' ` . ' ' " , . . .
--"` t 32q 1 67 g carbide target, which is also often maintained in a higher vacuum (lesser pressure~ target chamber. The NF3 can be ionized in either a radio freguency (r~), ~; microwave, direct current (DC) or electron cyclotron J'. 5 resonance (ECR) plasma, depending upon the desired c process.
Silicon carbide is chemically very inert and can only be conventionally etched by molten salts, or by chlorine or hydrogen gases at high ~ 10 temperatures. The dry etching techniques of the- present invention offer a more controllable low-temperature method of etching silicon carbide.
; As further stated above, however, previous attempts have shown that dry-etching silicon carbide using more conventional gases such as CF4 leaves a graphitic surface contaminated with materials such as fluorocarbon polymers. These surface conditions , are undesirable where the etched surface is being -~ prepared for making ohmic contacts for an electronic device.
~ Therefore, a desirable gas for etching ;~;1 silicon carbide should be readily dissociable into etching radicals and not into non-etching radicals, ~ ions or molecules which merely contaminate the `~ 25 target. Nitrogen trifluoride is one such desirable gas because it can be efficiently broken into ,J' nitrogen and free fluorine radicals, and because all i~ of the possible by-products of the ionization .~
process are volatile. As a result, surfaces etched with NF3 tend to be very clean. Where desired, the A~ NF3 can be mixed with other gases~ particularlyoxygen (2~ and argon (Ar~ in the method of the ; present invention.
`3: In particular embodiments of the present invention, thin films of beta silicon carbide which had been epitaxially grown on silicon (100) substrates were etched. As indicated in the J
.~~
''' ' ~ ' .", ' ' :~.
.
, . . : ~ .
, . . .
co-pending applications incorporated by reference, however, it is now possible to successfull~ grow device quality silicon carbide thin films upon -~ silicon carbide substrates and the etching techniques of the present inventio,n are equally applicable under these circumstancles.
Following the growth of the beta silicon ~` carbide thin films, the samples were polished with diamond paste, oxidized, etched in hydrofluoric acid, and rinsed in deionized water. The samples that were analyzed using scanning electron microscopy (SEM) were masked with evaporated aluminum that was patterned using standard photolithographic techniques. The samples used ~or Augex electron spectroscopy (AES) were left unmasked.
In a particular embodiment of the invention, the reactive ion etching techniques were performed in a parallel plate reactor with a 28.0 cm diameter aluminum anode, a 17.0 cm diameter anodized aluminum cathode, and a plate separation o~ 5.0 cm.
The samples were placed directly on the anodized aluminum cathode or, as discussed more ~ully herein, on a carbon cover plate over the anode. The samples were kept at temperatures of 308K. A 13.56 megahertz (MHz) rf supply powered the cathode at densities of 0.440 to 0.~48 watts per square centimeter (W/cm2). The chamber was evacuated to a pressure of 5 X 10-5 Torr and the NF3 was introduced at 25 standard cubic centimeters per minute (sccm) while the pressure was maintained at 40 millitorr ' (4x10-2 torr~. In general, flow rates of from about i 1 to about 500 sccm are appropriate with about 20 to about 60 sccm preferred. It should be understood that nitrogen trifluoride gas is an extremely toxic material and must be handled carefully and under the proper precautions in carrying out the techniques of the present invention.
As is known to those familiar with plasma science, a plasma can be formed uncler a number of gas pre~sure and electric power conditions. For example, natural lightning is a plzlsma effect which takes place at atmospheric pressure under the application of enormous amounts of electric power.
For scientific and commercial purposes, however, normally available power supplies make plasma formation much more feasible at lower gas pressures.
At moderate power supply l~vels (typically between about 10 and about 400 Watts to the powered electrode) a gas pressure of between about 5 and about 60 milliTorr (mTorr, i.e. between about 5x10-3 and 60x10-3 mTorr) are appropriately used, although in some cases, pressures high as 10 Torr are still appropriate. Using typical eguipment, this results in power densities of between about 0.04 and about 2 watts per square centimeter (W/cm2), with densities of between about 0.4 and about 0.9 W/cm2 preferred.
At generally lower pressures, the amount of gas present is insufficient to support the number of collisions required to maintain the plasma. At generally higher pressures, so much gas is present that the increased number of collisions tends to first dampen, and then quench, the plasma. It should be understood, therefore, that the selection of temperatures, power levels, and gas pressures used in practicing the present invention can vary widely and t~at those specified herein are given by way of example, and not as limitations on the scope of the invention.
Auger electron spectroscopy was used to analyze both the starting materials and the etched surfaces. Figure l(a) shows a typical AES spectrum for unetched beta silicon carbide, and indicates the .: , , ,~
". ~
.: :
.
~ i 1329167 presence of silicon, carbon, and oxygPn, present as a native oxide.
As stated earlier, a polymerization problem is commonly associated when halogenated hydrocarbons such as CF4 are used as the etchant.
This is illustrated by the AES spectra o~ Figures ~-~ 4(a~ and ~(b) which show a ~ignificant presence of ~' fluorine (~) on the etched surfaces. It has been discovered according to the present invention, however, that fluorine is the chief reactant for both silicon and carbon. ~his reaction scheme makes NF3 a desirable gas for etching SiC because it is moxe efficiently broken into free F radicals than are fluorinated hydrocarbons, and secondly because all of the possible by-products of its ionization ; are volatile. The practical advantages of these theoretical advantages were observed in the present invention in which etch rates were observed as fast .~i as 211 nanometers per minute (nm/min), which are the ` 20 highest etch rates ever reported for the dry etching :
of silicon carbide using any technique.
`:;
In the particular embodiment represented by Figures 3, 4 and 5, the reactive ion etching was carried out using an anodized aluminum cathode to ~` 25 support the SiC target. Under these conditions, ! however, there existed an apparent presence of some ~ aluminum oxide (A1203) on the etched surface, as ; demonstrated by the Auger electron spectrum of Figure 4(b). Additionally, the somewhat rough surface shown in the micrograph of Figure 5 ~as ~` observed foilowing the N~3 etching using the anodized aluminum cathode. Although applicant does not wish to be bound by any particular theory, it is believed ~;l that this results from Al203 which has sputtered from the cathode and masked small portions of the surface, a process referred to as nmicromasking."
The presence of iron (Fe) in the AES spectrum of ~' , i. .
,,, , :
: . .
; - 1329167 Figure l~b) and the rough surface seen in the micrograph of Figure 2 demonstrate the occurence of this same effect when a stainless steel cathode was used to support the target.
The presence of fluorine on the etched ; surface is also demonstrated by the AES spectrum in Figure 4~b). Presently, it is believed that the lack of reactivity between the anodized aluminum cathode and the fluorins species allows the fluorine ~i 10 species to undesirably accumulate and polymerize on the etched surfacs.
1.
Therefore, in order to eliminate the r. surface deposition of both fluorine and Al203, in a preferred embodiment of the invention a carbon cathode cover plate was placed in the RIE chamber.
Carbon has several advantages in the method of the present invention: it has a very low sputter yield, and it is reactive with fluorine. As is known to those familiar with these technologies, sputtering occurs when an ion strikes a surface knocking an atom, molecule or ion loose from that surface as a result of the energy imparted by the impinging ion.
1 This sputtered particle can be ejected from the cathode and deposit on the sur~ace being etched, leading to the undesired impurity or micromasking referred to earlier herPin. Of course, under certain circumstances, sputtering is a desired technique for depositing a particular material upon another material.
When the carbon cathode cover plate was used for the reactive ion etching of silicon carbide `~! in pure NF3, the greatly improved AES spectrum shown in Figure 6~b) resulted. This indicates that the surface is very clean, with no fluorine peak visible and only a minor amount of nitrogen present after etching. As stated above, the carbon in the cathode reacts with the fluorine, keeping the fluorine from i ;~~
.~. . .
, ~ .
~: .
, . ;
. .
,~ , :.: .
1 32q 1 67 accumulating and polymerizing upon the etched silicon carbide surface.
The differences between the use of the carbon cathode cover and the anodized aluminum cathode are demonstrated by Figure 5 (anodized aluminum cathode) and Figures 7, 8 and 9 which shows the smooth, etched surface of silicon carbide after reactive ion etching in CF4 (Figure 7) and in nitrogen trifluoride (Figures 8 and ~) using the carbon cathode.
Additionally, in spite of the use of carbon cathode in this embodiment, Figure 6(b) shows no significant increase in the carbon signal of the AES spectrum.
The invention thus demonstrates that in the reactive ion etching of silicon carbide, the choice of cathode material plays a major role in the chemical and physical characteristics of the etched surface. Because high quality ohmic contacts require both a smooth and a chemically clean surface, the invention provides an optimal configuration for dry etching of silicon carbide by using nitrogen trifluoride and a carbon cathode.
Given these characteristics, the invention comprises a method of patterning silicon carbide in the formation of electronic devices. By forming an appropriate masked pattern on the silicon carbide, etching it according to the present invention, and then removing the mask, desired patterns and devices can be fabricated.
In the specification, there have been set forth preferred and exemplary embodiments, which have been included by way of example and not limitation, the scope of the invention being set forth in the following claims:
-:: ; , , " .
. :, .
:':' ~ :
~ : . ' , ' ' ' ' .
Claims (32)
1. A method of etching a silicon carbide target, the method comprising:
applying a plasma generating potential across two electrodes;
generating a plasma between the two electrodes by introducing a gas between the electrodes, and wherein the gas is easily dissociated substantially into its elemental species in the plasma and wherein substantially all of the dissociated species from the gas are volatile in the plasma and wherein at least one of the dissociated species is reactive with silicon carbide; and positioning a silicon carbide target to be etched on one of the electrodes, and wherein the electrode is formed from a material with a low sputter yield and wherein the electrode material is reactive with the dissociated species; and reacting the plasma with the silicon carbide to thereby etch the silicon carbide, wherein the reaction of the dissociated species with the electrode, and the electrode's low sputter yield, prevent contamination of the target with either sputtered materials from the supporting electrode or unreacted dissociated species from the plasma.
applying a plasma generating potential across two electrodes;
generating a plasma between the two electrodes by introducing a gas between the electrodes, and wherein the gas is easily dissociated substantially into its elemental species in the plasma and wherein substantially all of the dissociated species from the gas are volatile in the plasma and wherein at least one of the dissociated species is reactive with silicon carbide; and positioning a silicon carbide target to be etched on one of the electrodes, and wherein the electrode is formed from a material with a low sputter yield and wherein the electrode material is reactive with the dissociated species; and reacting the plasma with the silicon carbide to thereby etch the silicon carbide, wherein the reaction of the dissociated species with the electrode, and the electrode's low sputter yield, prevent contamination of the target with either sputtered materials from the supporting electrode or unreacted dissociated species from the plasma.
2. A method according to Claim 1 wherein the step of generating a plasma comprises forming a reactive ion plasma from nitrogen trifluoride.
3. A method according to Claim 2 wherein the step of generating a reactive ion plasma comprises applying a direct current bias to the plasma.
4. A method according to Claim 1 wherein the step of positioning a silicon carbide target on one of the electrodes comprises positioning the silicon carbide target on the cathode.
5. A method according to Claim 4 wherein the step of positioning the silicon carbide target on the cathode comprises positioning the silicon carbide target on a carbon cathode.
6. A method according to Claim 1 wherein the step of positioning a silicon carbide target comprises positioning a silicon carbide thin film.
7. A method according to Claim 6 wherein the step of positioning a silicon carbide thin film comprises positioning a thin film of beta silicon carbide.
8. A method according to Claim 6 wherein the step of positioning a silicon carbide thin film comprises positioning a thin film of alpha silicon carbide.
9. A method according to Claim 1 wherein the step of applying a plasma generating potential comprises applying between about 10 and about 400 watts of power to the electrodes.
10. A method according to Claim 1 wherein the step of applying a plasma generating potential comprises applying a power density of between about 0.04 and about 2 watts per square centimeter to the powered electrode.
11. A method according to Claim 1 wherein the step of applying a plasma generating potential comprises applying a power density of between about 0.4 and about 0.9 watts per square centimeter to the powered electrode.
12. A method according to Claim 1 wherein the step of introducing a gas between the electrodes comprises introducing the gas at a pressure of between about 5 milliTorr and about 10 Torr.
13. A method according to Claim 1 wherein the step of introducing a gas between the electrodes comprises introducing the gas at a pressure of about 40 milliTorr.
14. A method according to Claim 1 wherein the step of introducing a gas comprises introducing a gas at a flow rate of between about 1 and about 500 standard cubic centimeters per minute.
15. A method according to Claim 1 wherein the step of introducing a gas comprises introducing a gas at a flow rate of between about 20 and about 60 standard cubic centimeters per minute.
16. A method according to Claim 1 wherein the step of introducing a gas comprises introducing a gas at a flow rate of about 25 standard cubic centimeters per minute.
17. A method according to Claim 1 wherein the step of introducing a gas comprises introducing a mixture of nitrogen trifluoride and oxygen.
18. A method according to Claim 1 wherein the step of introducing a gas comprises introducing a mixture of nitrogen trifluoride and argon.
19. A method according to Claim 1 wherein the step of introducing a gas comprises introducing a mixture of nitrogen trifluoride, oxygen and argon.
20. A method of etching of a silicon carbide target comprising:
applying a plasma generating potential across an anode and a carbon cathode;
generating a plasma between the anode and the carbon cathode by introducing nitrogen trifluoride therebetween;
positioning a silicon carbide target to be etched on the carbon cathode whereby the carbon cathode exhibits a low sputter yield and is reactive with dissociated fluorine from the nitrogen trifluoride; and reacting the plasma with the silicon carbide to thereby etch the silicon carbide, wherein the reaction of dissociated fluorine with the carbon cathode, and the cathode's low sputter yield, prevent contamination of the target with either sputtered carbon materials from the cathode or polymerized fluorine species from the plasma.
applying a plasma generating potential across an anode and a carbon cathode;
generating a plasma between the anode and the carbon cathode by introducing nitrogen trifluoride therebetween;
positioning a silicon carbide target to be etched on the carbon cathode whereby the carbon cathode exhibits a low sputter yield and is reactive with dissociated fluorine from the nitrogen trifluoride; and reacting the plasma with the silicon carbide to thereby etch the silicon carbide, wherein the reaction of dissociated fluorine with the carbon cathode, and the cathode's low sputter yield, prevent contamination of the target with either sputtered carbon materials from the cathode or polymerized fluorine species from the plasma.
21. A method according to Claim 20 wherein the step of positioning a silicon carbide target comprises positioning a doped silicon carbide target.
22. A method according to Claim 21 wherein the step of positioning a doped silicon carbide target comprises positioning a doped beta silicon carbide target.
23. A method according to Claim 21 wherein the step of positioning a doped silicon carbide target comprises positioning a doped alpha silicon carbide target.
24. A method according to Claim 20 wherein the step of generating a plasma further comprises applying a direct current bias to the plasma.
25. A method of reactive ion beam etching of a silicon carbide target comprising:
applying a plasma generating potential and a direct current bias across two electrodes positioned in a source chamber;
generating a reactive ion plasma between the two electrodes in the source chamber by introducing a gas which is easily dissociated into its elemental species in the plasma and wherein substantially all of the dissociated species are volatile in the plasma and wherein at least one of the species is reactive with silicon carbide;
positioning a silicon carbide target in a target chamber on a support formed from a material with a low sputter yield and wherein the material reacts with the elemental species in the plasma to thereby prevent contamination of the target with either sputtered materials from the support or polymerized species from the plasma, and wherein the target chamber is in communication with the source chamber; and applying a negative bias to the target so that a reactive ion plasma beam is directed from the source chamber to the target chamber to thereby etch the silicon carbide target.
applying a plasma generating potential and a direct current bias across two electrodes positioned in a source chamber;
generating a reactive ion plasma between the two electrodes in the source chamber by introducing a gas which is easily dissociated into its elemental species in the plasma and wherein substantially all of the dissociated species are volatile in the plasma and wherein at least one of the species is reactive with silicon carbide;
positioning a silicon carbide target in a target chamber on a support formed from a material with a low sputter yield and wherein the material reacts with the elemental species in the plasma to thereby prevent contamination of the target with either sputtered materials from the support or polymerized species from the plasma, and wherein the target chamber is in communication with the source chamber; and applying a negative bias to the target so that a reactive ion plasma beam is directed from the source chamber to the target chamber to thereby etch the silicon carbide target.
26. A method according to Claim 25 wherein the step of introducing a gas comprises introducing nitrogen trifluoride.
27. A method according to Claim 25 wherein the step of positioning a silicon carbide target comprises positioning the silicon carbide target on a carbon support.
28. A method according to Claim 25 further comprising maintaining the target chamber at a lesser pressure than the source chamber.
29. A method of patterning silicon carbide in the formation of electronic devices using reactive ion etching, the method comprising forming a masked pattern on a silicon carbide substrate;
positioning the masked silicon carbide substrate as a target on a cathode in a reactive ion plasma system having an anode opposite the cathode;
and applying a plasma generating potential and a direct current bias across the anode and cathode in the reactive ion system;
generating plasma in the system by introducing a gas which is easily dissociated in the plasma and wherein substantially all of the dissociated species are volatile in the plasma and wherein at least one of the dissociated species is reactive with silicon carbide;
wherein the cathode is formed from a material with a low sputter yield and wherein the material reacts with the dissociated species in the plasma to thereby prevent contamination of the target with either sputtered materials from the cathode or polymerized species from the plasma; and reacting the plasma with the silicon carbide substrate to thereby etch the silicon carbide.
positioning the masked silicon carbide substrate as a target on a cathode in a reactive ion plasma system having an anode opposite the cathode;
and applying a plasma generating potential and a direct current bias across the anode and cathode in the reactive ion system;
generating plasma in the system by introducing a gas which is easily dissociated in the plasma and wherein substantially all of the dissociated species are volatile in the plasma and wherein at least one of the dissociated species is reactive with silicon carbide;
wherein the cathode is formed from a material with a low sputter yield and wherein the material reacts with the dissociated species in the plasma to thereby prevent contamination of the target with either sputtered materials from the cathode or polymerized species from the plasma; and reacting the plasma with the silicon carbide substrate to thereby etch the silicon carbide.
30. A method according to Claim 29 further comprising the step of removing the mask from the silicon carbide substrate following the step of reacting the plasma with the silicon carbide.
31. A method according to Claim 29 wherein the step of introducing a gas comprises introducing nitrogen trifluoride.
32. A method according to Claim 29 wherein the step of positioning the silicon carbide masked substrate on the cathode comprises positioning the masked silicon carbide substrate on a carbon cathode.