US20020090761A1 - Package with low stress hermetic seal - Google Patents
Package with low stress hermetic seal Download PDFInfo
- Publication number
- US20020090761A1 US20020090761A1 US10/054,099 US5409902A US2002090761A1 US 20020090761 A1 US20020090761 A1 US 20020090761A1 US 5409902 A US5409902 A US 5409902A US 2002090761 A1 US2002090761 A1 US 2002090761A1
- Authority
- US
- United States
- Prior art keywords
- substrate
- frame
- cover
- seal
- solder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- 1. Field of the Invention
- This invention relates to semiconductor packages and more particularly to methods for hermetically sealing such packages and to the resultant hermetically sealed packages.
- 2. Description of Related Art
- FIG. 1 is a schematic diagram of a cross-section of a fragment of a
semiconductor module 10 of the kind shown in U.S. Pat. No. 6,046,074 of D. C. McHerron and H. T. Toy, commonly assigned, for “Hermetic Thin Film Metallized Sealband for SCM and MCM-D Modules”. FIG. 1 illustrates a common method of hermetically sealing a protective cap 12 (with atop 13 and withsides 27 which have vertical sidewalls 28) to achip carrier 14 with asealing structure 31 at the periphery of thechip carrier 14. Thesealing structure 31 comprises a layer ofsolder 52 between a thin film (carrier)sealband 32 and acap sealband 42. The cover andcarrier sealbands 32/42, which are composed of sequentially applied thin metal sealing layers, are hermetically sealed together by thesolder layer 52. The all metalperipheral sealing structure 31 transmits high stress to thetop surface 14T of thechip carrier 14, due to the rigidity of thesolder 52 and thesealbands 32/42 and due to the thermal expansivity mismatch between the metals in thesealing structure 31 and thechip carrier 14, e.g. a ceramic chip carrier. On the one hand, thechip carrier 14 can be composed of relatively strong materials such as alumina ceramics which are able to withstand the high stress. On the other hand, weaker materials such as glass-ceramics may develop stress cracks along the periphery of theseal 31 from sealing or from subsequent thermal cycling. Therefore, for such relatively weak materials as glass-ceramics, the problem is to devise a relatively inexpensive method for hermetically sealing aprotective cap 12 to achip carrier 14 where stress transmitted to thechip carrier 14 is a major issue. - Japanese Patent JP6140527 deals with hermetic sealing device component, wherein an A/N (Aluminum Nitride) circuit substrate is connected by brazing it to a metal frame while interposing a soft metal frame member.
- IBM TDB Vol. 29, No. 11, April 1987, p 5088, of Arndt et al., “Flexible Leaded Chip Carrier” describes a second level attachment process for replacing pins with a flexible connection from TSM (Top Surface Mounted) surface pads which wind around the sides of the ceramic base plate (substrate) to the bottom of the ceramic base plate. A ceramic lid assures an hermetically sealed package”. A flexible polyimide (PI) lead minimizes stress on the surface solder board connection. The ceramic base plate provides dimensional stability.
- U.S. Pat. No. 5,881,945, Edwards et al. “Multi-Layer Solder Seal Band for Semiconductor Substrates and Process”, commonly assigned, describes a multilayer three layer, all metallic sealing structure, but specifies all layers of the seal are metal in which the height of the seal is increased. The thick middle layer of the sealing structure, which has a relatively higher melting point than the outer layers, can be a lead/tin, lead/indium or tin/bismuth solder material. The top and bottom layers of the sealing structure, which have a relatively lower melting point than the middle layer can be lead/tin, lead/indium, or tin/bismuth solder materials. This makes the sealing structure more resistant to fatigue from CTE (Coefficient of Thermal Expansion) mismatch between the cap and the carrier. We have found that this type of sealing structure can cause substrate cracks adjacent to the seal band when a weaker substrate material such as glass-ceramic is used.
- U.S. Pat. No. 5,201,456, Reynal et al. “Process for Assembly of a Metal Can on a Substrate Bearing an Integrated Circuit” U.S. Pat. No. 5,201,456 teaches sealing a metal can to a substrate with a multi-layer seal. The metal can is formed by a metal frame with a metal cap sealed thereto by welding. The seal is comprised of a dielectric layer, a transition layer, and a metal layer. The transition layer is a mixture, of dielectric and metal (approximately 50/50). The purpose is to provide an “air-tight”, stress resistant seal and to provide electrical isolation of the lid from underlying conductive lines (“strip conductors”). The seal contains conductive lines.
- U.S. Pat. No. 5,069,978 Mizuhara “Brazed Composite Having Interlayer of Expanded Metal” teaches brazing plates (e.g. chip carrier and cover) of dissimilar materials with a metal interlayer. The interlayer is formed into a slit, creased geometry, such that it offers a compliant connection, and is brazed on either side to the two plates. At any rate, it talks nothing about dual seal bands or polymers.
- U.S. Pat. No. 4,315,591, Houston, “Method for Thermo-Compression Diffusion Bonding A Structured Copper Strain Buffer to Each Side of a Substrateless Semiconductor Wafer” teaches a thermo-compression diffusion bonding process whereby copper strain buffers are attached to opposite sides of a wafer.
- IBM TDB Vol. 27, No. 3, (August 1984) p 1701, of Olah et al. “Hermetic Seal for Semiconductor Package” describes a process for attaching non-metallic gaskets hermetically to porous substrates by mechanically clamping.
- IBM TDB Vol. 27, No. 1A (June 1984), p. 129, of Bakos et al. “Method for Low Temperature Module Encapsulation” describes a U-channel sealing scheme, with a low melt solder fill. The bismuth-based solder composition specified has a negative CTE, so that on cooling additional pressure is applied to the inside of the channel and the legs of the cap.
- U.S. Pat. No. 5,931,222 of Toy, Edwards, Shih and Giri for “Adhesion Promoting Layer for Bonding Polymeric Adhesive to Metal and a Heat Sink Assembly Using Same” describes adhesion of a heat sink to the top surface of a nickel plated metal cap. The heat sink is adapted for cooling chips on a chip carrier. A hermetic sealing structure is formed at bottom edges of the cap which are nickel plated to the multi-chip carrier. A bottom seal band of nickel/gold layers is formed on the top surface of the chip carrier. The seal is formed by lead/tin solder between the nickel plated surface of the cap and the bottom seal band on the chip carrier. For the heat sink, the top of the cap is coated with a thin adhesion promoting metal film such as chromium or titanium. The heat sink is attached in a non-hermetic fashion to the thin adhesion-promoting metal film by a polymeric heat sink adhesive, such as a silicone elastomer material, which provides an interfacial bond between the top of the cap and a polymeric adhesive.
- Previous glass-ceramic products which required hermetic sealing have used mechanical seals, such as solder coated C-rings. With associated required hardware, these tend to be more expensive and require more board real estate than the present invention. Also a C-ring seal requires an ultra-flat surface which translates to an expensive surface planarization process. In the present invention the thicker solder later (perhaps 100 micrometers) is able to absorb substrate out-of-flatness.
- Unlike Japanese Patent JP6140527, this invention does not involve a frame, but replaces a “soft metal” (presumably a soft solder) with a thin stress-absorbent polymer, which is nearly hermetic, and can be made fully hermetic with a solder filled channel through the polymer.
- As contrasted with U.S. Pat. No. 5,881,945, Edwards et al., a polymer layer is positioned adjacent to the chip carrier.
- This invention differs from U.S. Pat. No. 5,201,456 of Reynal et al. in several regards as follows:
- 1. The surface to which sealing is made contains no conductive lines or features.
- 2. The seal contains just a polymer and metal without any transition layer.
- 3. This invention includes the option of having one layer “shared” by the metal and polymer via a channel.
- Hermetic sealing has been an established art for the most common electronic chip carrier materials, but remains an expensive real-estate-costly process for glass-ceramic until this invention.
- In accordance with this invention, a method is provided for forming a sealed electronic circuit package comprising the following steps. Provide a substrate having a top surface and a cover having a mating surface confronting the top surface of the substrate. Form a seal at the peripheral edge of the substrate between the substrate and the mating surface of the cover by the following steps. Forming a peripheral substrate non-metallic soft frame formed on the top surface of the substrate having a top soft frame surface which faces upwardly. Provide cover frame surface on the mating surface of the cover which is exposed downwardly. Form a lower adhesion frame over the soft frame, and join the top surface of the lower adhesion frame and the cover frame surface with solder to form a hermetic via-seal to the substrate frame surface forming a seal between the cover frame surface and the substrate.
- One can employ a solder selected from the group consisting of an (SnAg or a SnAgCu solder with about 96% Sn) or a two-material (lead/tin eutectic) solder plus a polymer seal instead of a channel filled with solder.
- Preferably, the solder has a melting point 30° C. to 40° C. below the melting point or the glass transition temperature Tg of any polymer or the melting point of any solder in the module or package.
- Preferably, the channel and the via-seal are located laterally aside from the confronting portions of the surfaces of the cover and the substrate; the via-seal is exposed on the surface of the soft layer on an exterior surface of the peripheral substrate frame; or the via-seal is exposed on the surface of the soft layer on an interior surface of the peripheral substrate frame; the substrate is a ceramic chip carrier and the soft layer is a polymer; the substrate is a ceramic or glass ceramic chip carrier and the soft layer is a polymer, preferably polyimide; the lower adhesion frame is composed of laminated Cr—Ni—Au layers; the soft layer has a thickness preferably less than or equal to about 12 μm.
- Preferably, form the non-metallic soft frame with a central channel extending down through the non-metallic soft layer to expose a portion of the substrate frame surface below the channel with the lower adhesion frame extending down through the channel formed in the non-metallic soft layer to contact the substrate surface, whereby the hermetic via-seal extends through the channel to the substrate frame surface to form a seal between the cover frame surface and the substrate.
- Preferably, form the lower adhesion frame with an extension across the edge of the non-metallic soft layer to contact the substrate surface at a distal location, so the hermetic via-seal extends across the edge of the soft layer to form a seal between the cover frame surface and the substrate.
- In accordance with another aspect of this invention, the method comprises forming a sealed electronic circuit package by providing a substrate having a top surface and a cover having a mating surface confronting the top surface of the substrate. Form a seal at the peripheral edge of the substrate between the substrate and the mating surface of the cover by the following steps. Form a peripheral substrate non-metallic soft frame formed on the top surface of the substrate having a top soft frame surface which faces upwardly with a central channel formed down through the non-metallic soft layer to expose a portion of the substrate frame surface below the channel. Form a cover frame for providing adhesion formed on the mating surface of the cover, the cover frame having a cover frame surface which is exposed downwardly. Form a lower adhesion frame over the soft frame extending down through the channel formed in the non-metallic soft layer to contact the substrate surface. Join the top surface of the lower adhesion frame and the cover frame surface with solder and extending into the channel to form a hermetic via-seal through the channel to the substrate frame surface form a seal between the cover frame surface and the substrate extending through the channel in the soft frame.
- One can employ a solder selected from the group consisting of an (SnAg or a SnAgCu solder with about 96% Sn) or a two-material (lead/tin eutectic) solder plus a polymer seal instead of a channel filled with solder.
- Preferably, the solder has a melting point 30° C. to 40° C. below the melting point or the glass transition temperature Tg of any polymer or the melting point of any solder in the module or package.
- In accordance with another aspect of this invention sealed electronic circuit package is provided comprising a substrate having a top surface, a cover having a mating surface confronting the top surface of the substrate, a seal at the peripheral edge of the substrate between the substrate and the mating surface of the cover. The seal includes a peripheral substrate non-metallic soft frame formed on the top surface of the substrate having a top soft frame surface which faces upwardly, a cover frame for providing adhesion formed on the mating surface of the cover, the cover frame having a cover frame surface which is exposed downwardly, a lower adhesion frame formed over the soft frame extending, and solder joining the top surface of the lower adhesion frame and the cover frame surface to form a hermetic via-seal.
- Preferably the channel and the via-seal are located laterally aside from the confronting surfaces of the cover and substrate; with the via-seal exposed on the surface of the soft layer on an exterior surface of the peripheral substrate frame; the via-seal is exposed on the surface of the soft layer on an interior surface of the peripheral substrate frame; the substrate is a ceramic or glass ceramic chip carrier and the soft layer is a polymer preferably comprising polyimide; the lower adhesion frame is composed of laminated Cr—Ni—Au layers; and the soft layer has a thickness less than or equal to about 12 μm. Preferably the non-metallic soft frame having a central channel formed down through the non-metallic soft layer to expose a portion of the substrate frame surface below the channel with the lower adhesion frame extending down through the channel formed in the non-metallic soft layer to contact the substrate surface, whereby the hermetic via-seal extends through the channel to the substrate frame surface to form a seal between the cover frame surface and the substrate. Preferably, the lower adhesion frame extends across the edge of the non-metallic soft layer to contact the substrate surface at a distal location, whereby the hermetic via-seal extends across the edge of the soft layer to form a seal between the cover frame surface and the substrate.
- One can employ a solder selected from the group consisting of an (SnAg or a SnAgCu solder with about 96% Sn) or a two-material (lead/tin eutectic) solder plus a polymer seal instead of a channel filled with solder.
- Preferably, the solder has a melting point 30° C. to 40° C. below the melting point or the glass transition temperature Tg of any polymer or the melting point of any solder in the module or package.
- In accordance with another aspect of this invention, a sealed electronic circuit package comprises a substrate having a top surface, a cover having a mating surface confronting the top surface of the substrate, a seal at the peripheral edge of the substrate between the substrate and the mating surface of the cover, the seal including a)a non-metallic soft layer formed the top surface of the substrate for providing adhesion, at the peripheral edge of the substrate, the substrate frame having a top surface facing upwardly, b) a cover frame for providing adhesion formed on the mating surface of the cover having a cover frame surface facing downwardly, c) an intermediate adhesion layer formed on the upper surface of the soft layer, the intermediate adhesion layer having an upper surface, and d) solder formed between the intermediate adhesion layer upper surface and the cover frame surface.
- Preferably the sealed electronic circuit package comprises a substrate having a top surface, a cover having a mating surface confronting the top surface of the substrate, a seal at the peripheral edge of the substrate between the substrate and the mating surface of the cover. The seal includes a) a peripheral substrate non-metallic soft frame formed on the top surface of the substrate having a top soft frame surface which faces upwardly with a central channel formed down through the non-metallic soft layer to expose a portion of the substrate frame surface below the channel, b) a cover frame for providing adhesion formed on the mating surface of the cover, the cover frame having a cover frame surface which is exposed downwardly, c) a lower adhesion frame formed over the soft frame extending down through the channel formed in the non-metallic soft layer to contact the substrate surface, and d) solder joining the top surface of the lower adhesion frame and the cover frame surface and extending into the channel to form a hermetic via-seal through the channel to the substrate frame surface form a seal between the cover frame surface and the substrate extending through the channel in the soft frame.
- The foregoing and other aspects and advantages of this invention are explained and described below with reference to the accompanying drawings, in which:
- FIG. 1 is a schematic diagram of a cross-section of a fragment of a semiconductor prior art module.
- FIG. 2 is a schematic diagram a cross-section of a fragment of a semiconductor module illustrating the structure of a hermetic sealing structure with a central sealing channel in accordance with a preferred embodiment of this invention.
- FIGS.3A-3E show the process flow for formation of the semiconductor module illustrating of FIG. 2. with a hermetic sealing structure of FIG. 2 in accordance with this invention.
- FIG. 3A is a sectional view of the device of FIG. 2 in an early stage of the process after formation of a soft, polymeric cushion-frame on the surface of the chip carrier.
- FIG. 3B shows the device of FIG. 3A after formation of a central channel in the soft, polymeric cushion-frame.
- FIG. 3C shows the device of FIG. 3B after formation of a thin metal lower adhesion frame on the surface of the soft, polymeric cushion-frame which conforms to the surface of cushion-frame extending down into and across the central channel.
- FIG. 3D shows the device of FIG. 3B after a solder frame preform has been placed upon the upper surface of the thin metal lower adhesion frame leaving an upper, via-seal channel directly above the central channel.
- FIG. 3E shows the device of FIG. 3D after a solid, solder-frame preform has been heated above its melting point to form a molded solder frame providing the hermetic seal seen in FIG. 2.
- FIG. 4A is a schematic diagram of the semiconductor module of FIG. 3A showing a plan view of an example of a soft, non-metallic, polymer cushion-frame formed on the surface of a chip carrier on a substantially reduced scale from FIG. 3A
- FIG. 4B shows, the semiconductor module of FIG. 4A after the soft, non-metallic, polymer cushion-frame has been grooved to form a contact channel by ablation of a channel lengthwise, down the center of the four walls of the polymer frame, as seen in FIG. 3B.
- FIG. 4C shows the semiconductor module of FIG. 4A after the formation of a first layer of the adhesion frame with the first layer of the adhesion frame covering the left and bottom portions of the cushion-frame.
- FIG. 4D shows the semiconductor module of FIG. 4C after the formation of a second layer of the adhesion frame with the second layer covering the right and top portions of the cushion-frame with an overlap at the upper left and lower right comers as seen in FIG. 3C.
- FIG. 4E shows the semiconductor module of FIG. 4D after addition of a solid, solder-frame preform to the top surfaces of the lower adhesion frame bridging across the via-seal channel, since the solder is in its solid form and the addition of one or several chips with C4 solder balls resting on the vias in the semiconductor module as seen in FIG. 3D. FIG. 4E shows the view of the module preceding heating of the solder preform to create the solder frame providing the hermetic seal seen in FIGS. 2 and 3E.
- FIG. 5A shows a modification of the embodiment of FIG. 2 in which a solder seal is offset (inboard, but could just as well be outboard) from a metal/chip carrier contact via-seal.
- FIG. 5B shows a modification of the embodiment of FIG. 5A in which a solder seal is offset outboard from a metal/chip carrier contact via-seal. All of the elements of the module of FIG.6 are otherwise the same as in FIG. 5.
- FIG. 6 shows a simple, “nearly hermetic” embodiment of the device of FIG. 2, with the ablated channel of FIGS. 3B and 4B and with the channel of FIG. 2 eliminated entirely.
- FIG. 2 is a schematic diagram a cross-section of a fragment of a
semiconductor module 100 illustrating the structure of a preferred embodiment of this invention. Themodule 100 includes achip carrier 114 and a rectangularly shapedchip cover 112, fragments of which are shown bonded together. Thechip cover 112 has a top 113 and fourvertical sides 127. Thesides 127, which havevertical sidewalls 128, are joined at their bottoms surfaces to the periphery of the top surface of thechip carrier 114 by ahermetic sealing structure 131. That is to say that theehermetic sealing structure 131 is formed between bottoms of thesides 127 ofcover 112 and the border of the top surface of thechip carrier 114, in accordance with this invention. A via-seal 156 is formed bysolder 152 which is located in a position that is remote from the high-stress edges of thelower adhesion frame 132. Thesolder 152 which fills a narrow via-seal channel 155 is separated from the high-stress edges of thelower adhesion frame 132 by a soft, polymeric cushion-frame 54. This separation between the solder and the high stress edges is provided to protect thechip carrier 114 from the stresses generated between the solder and the high stress edges of thelower adhesion frame 132. - Inside the
cover 112, a electronic-circuit-bearing,semiconductor chip 20 is shown supported by anoptional interconnect structure 21 which is formed on the surface of thechip carrier 114. In this embodiment, theinterconnect structure 21 comprises an insulatinglayer 22 which hasmetal vias 23 extending from the top surface oflayer 22 to contacts (not shown) in thechip carrier 114. The chip 20 (which may represent just one of a plurality ofchips 20 formed in an x-y array as seen in FIG. 4E, is connected to thevias 23 in theinterconnect structure 21 by connectors which are shown as C4solder ball junctions 24 in this embodiment of the invention. - The
hermetic sealing structure 131 is provided to protect the chip or a plurality ofchips 20 or other elements and the circuits on the surface of thechip carrier 114 which need to protected from the ambient atmosphere outside of themodule 100. - FIGS.3A-3E illustrate the process flow of forming the
hermetic sealing structure 131 of FIG. 2 in accordance with this invention. - FIG. 3A is a sectional view of the
device 100 of FIG. 2 in an early stage of the process after formation of a soft, polymeric cushion-frame 54 on the surface of thechip carrier 114. - FIG. 3B shows the
device 100 of FIG. 3A after formation of acentral channel 55C in the soft, polymeric cushion-frame 54. The soft, polymeric cushion-frame 54 (preferably a material such as polyimide) is formed directly upon thechip carrier 114. The soft, polymeric cushion-frame 54 and the metallower adhesion frame 132 provide physical separation and decoupling of thesolder frame preform 152 in the sealingstructure 131 from thechip carrier 114. - FIG. 3C shows the
device 100 of FIG. 3B after formation of a thin metallower adhesion frame 132 on the surface of the soft, polymeric cushion-frame 54 which conforms to the surface of cushion-frame 54 extending down into and across thecentral channel 55C, forming an upper, via-seal channel 155. The via-seal channel 155 (which provides space forsolder 152 in FIGS. 2 and 3E) is formed by projection of the metallower adhesion frame 132 through the contact channel S5C (shown in FIG. 3B as mentioned above) in the center of the soft, polymeric cushion-frame 54. Thus a hermetic seal is provided by the metal tosubstrate contact 132C since the thin metallower adhesion frame 132 directly contacts thechip carrier 114. - FIG. 3D shows the
device 100 of FIG. 3B after asolder frame preform 152 has been placed upon the upper surface of the thin metallower adhesion frame 132 leaving an upper, via-seal channel 155 directly above thecentral channel 55C. - FIG. 3E shows the
device 100 of FIG. 3D after thesolder frame preform 152 has been heated to its melting point so that thesolder frame preform 152 melts and flows down into the upper, via-seal channel 155 (shown in FIGS. 3C and 3D) forming asolder frame 152′ conforming with the surface of the metallower adhesion frame 132. A metalcover adhesion frame 142, which is formed on the bottom of thesides 127 of thecover 112, is bonded to thesolder frame 152′. Thesolder frame 152′, which fills the via-seal channel 155 has formed a metal via-seal 156 is formed in thechannel 155 by the heating of thesolder frame preform 152 until it melts thereby filling the via-seal channel 155 midway between the outer and inner edges of the soft, polymeric cushion-frame 54. Thesolder frame 152′ forms the metal-to-metal via-seal 156 in thechannel 155 above the thin metallower adhesion frame 132. Note that the metalcover adhesion frame 142 is formed on the bottom surfaces at the bases of the foursides 127 of thecap 112 confronting thesolder frame preform 152 and thus provides full hermeticity. The via-seal 156, formed by thesolder frame 152′ filling the via-seal channel 155, is narrow and the separation provided by the soft, polymeric cushion-frame 54 protects thechip carrier 114 which is remote from the high-stress edges of thelower adhesion frame 132 as can be seen by reference to FIGS. 3A-3C and the text relative found herein below. - Note that the
solder frame 152′ straddles thecontact channel 55C, distancing the edges of thesolder frame 152′ from thelower adhesion frame 132 which extends through thepolymeric layer 54. In addition, thesolder frame preform 152 has a low melting point relative to the glass transition temperature Tg of thepolymeric layer 54. As used herein, the glass transition temperature Tg of a polymer is the temperature above which there is a sudden change in the chain mobility of a polymer. - FIGS.3A-3E show the process flow for formation of the device shown in FIG. 2.
- FIG. 3A is a sectional
view showing module 100 in an intermediate stage of the process which produces themodule 100 of FIG. 2. Aninterconnect structure 21 is shown which comprises an insulatinglayer 22 with metal, electricallyconductive vias 23 therethrough extending from the top surface of the insulatinglayer 22 to contacts (not shown) in thechip carrier 21. - To the right of the
interconnect structure 21 is shown a layer of a soft, non-metallic, polymeric cushion-frame 54 which has been formed on the polished surface of thechip carrier 114. The soft, non-metallic, polymeric cushion-frame 54 preferably comprises a material such as polyimide. - FIG. 4A is a schematic diagram showing a plan view of an example of a cushion-
frame 54 formed on the surface of achip carrier 114 on a substantially reduced scale from FIG. 3A. - The cushion-
frame 54 is deposited selectively to form the pattern seen in FIG. 3A and FIG. 4A by screen printing or by fabrication as one of the layers employed for providing connections for the C4 solder balls to thecarrier 114. It should be noted that for this 20 invention it is not necessary for the dimensions of the cushion-frame 54 to be commensurate with the layers formed thereon which may be narrower. - In FIG. 3B and FIG. 4B, the
module 100 is shown after the soft, non-metallic, polymer cushion-frame 54 has been grooved to form thecontact channel 55C by ablation of a channel lengthwise, down the center of the four walls of the polymer frame. The ablation process is preferably performed using an excimer laser at a frequency of 308 nm. Then themodule 100 is exposed to an oxygen plasma to remove the layer of debris left by the ablation process. Thetrench 55C has taperedsidewalls 55W formed in the soft, polymeric, cushion-frame 54 so that thetrench 55C is narrower at the exposedtop surface 114T of thechip carrier 114 than at the top surface of the polymer cushion-frame 54. - FIG. 4B is a schematic diagram showing a plan view of an example of the cushion-
frame 54 of FIG. 4A after ablation of achannel 55C exposing thetop surface 114T of achip carrier 114 in the center of the cushion-frame 54. The tapered sidewalls 55W are indicated by the thick lines on the sides of thechannel 55C. - FIG. 4C shows the result of forming the
first layer 132A of theadhesion frame 132 which covers the left and bottom portions of the cushion-frame 54. - FIG. 4D shows the result of forming the
second portion 132B of theadhesion frame layer 132 with thesecond portion 132B covering the right and top portions of the cushion-frame 54, overlapping withfirst portion 132A at the upper left and lower right comers since the mask used for the evaporation extends to the full x and y dimensions of the completedadhesion frame 132. - FIG. 3C shows the
module 100 after the formation of the metal,lower adhesion frame 132 composed to two overlappingcomplementary patterns entire frame 132. - The metal,
lower adhesion frame 132 is preferably composed of Cr/Ni/Au adhesion layers or another suitable combination. - FIGS. 3D and 4E show the
module 100 after addition of a solid, solder-frame preform 152 to the top surfaces of thelower adhesion frame 132 bridging across the via-seal channel 155 since the solder is in its solid form and the addition of one orseveral chips 20 withC4 solder balls 24 resting on thevias 23 in thestructure 22. - FIGS. 3E shows the
module 100 after the solder-frame preform 152 has been reshaped by heating above the melting point of the solder-frame preform 152 to fill the via-seal channel 155 coming into contact with the remainder of the surface of thelower adhesion frame 132. It should be pointed out at this point that the melting and consequent reshaping of the solder-frame preform 152 is usually performed serially, but under rare circumstances can be performed in parallel with the forming of C4 solder bonds to thevias 23. - The reshaped solder-
frame 152 combined with thelower adhesion frame 132 form a metal structure reaching down through thechannel 55C in the soft cushion-frame 54 to contact thechip carrier 114. - The method used to apply the solder to the surface of the soft layer structure is to flux the lower adhesion frame (sealband)132. Then the is placed over the fluxed
sealband 132. Next, the module 100 (without its cover which is to be added later) is placed in a furnace to reflow the solder in the solder-frame preform 152. Then the part is cleaned. - In FIG. 3E, the
module 100 is shown after the joining of thecover 112 and thecover adhesion frame 142 to the solder-frame preform 152. Thecover adhesion frame 142 is bonded to the carrier of thesidewall 128 of thecap 112 prior to joining thecover 112 to the solder-frame preform 152. Thecover adhesion frame 142 may be composed of layers comprising Ni—Au or another suitable combination, as described above. - The
cover 112 is positioned with the metal cover adhesion frame resting on thesolder preform 152. Then themodule 100 is heated above the melting point of thepreform 152 to provide a hermetically sealed bond between the metallower adhesion frame 132 and the metalcover adhesion frame 142. Thus the metalcover adhesion frame 142 on the bottom surface at the base ofvertical sidewall 128 of thecap 112 is bonded to the top surface of thesolder frame preform 152 and thus provides full hermeticity. - Alternatively, the solder-
frame preform 152 or its equivalent can be secured to thecap 112 instead of the above described process; or the solder may be cast onto the cap instead of being joined as a preform. - The method used to apply the cap (lid)112 to the surface of the
solder layer 152 is to fixture thelid 112 to the sealband. A load is applied to a pressure of about two pounds. Then the fixtured assembly is placed in a furnace to reflow thesolder 152. - The environmental conditions are required to assure that the environment within the package is clean prior to sealing the cap (lid)112 to the
solder layer 152 is for the substrate chip assembly (module 100) which has flux applied is cleaned with a solvent such as xylene or turpene, followed by rinsing in IPA (IsoPropyl Alcohol), DI (deionized) water followed by nitrogen gas (N2) drying and bake operations. - FIG. 5A shows a modification of the embodiment of FIG. 2 in which a
solder seal 431 is offset (inboard, but could just as well be outboard) from a metal/chip carrier contact via-seal 458. In this case the via-seal 458 contacts thechip carrier 414 at a distal location on the exterior (outboard) periphery of the polyimide PI polymer cushion-frame 454. As in FIG. 2, themodule 400 includes achip carrier 414 and a chip cover 412 (fragments of which are shown) bonded together and hermetically sealed by a sealingstructure 431 in accordance with this invention. Thechip carrier 414 supports aninterconnect structure 22 andchips 20 as described above. - The chip cover412 has a top 413 and four
vertical sides 427. Thesides 427 havevertical sidewalls 428 which are joined to thechip carrier 414 by ahermetic sealing structure 431. Thehermetic sealing structure 431 is formed between thesides 427 of cover 412 and thechip carrier 414, in accordance with this invention. A metalcover adhesion frame 442 is formed on the bottom of thevertical sides 427 of the cover. The metalcover adhesion frame 442 may be composed of layers comprising Mo—Ni—Au or another suitable combination, as described above. - The sealing
structure 431 employs a soft, polymeric cushion-frame 454 formed on the surface of thechip carrier 414. - A metal
lower adhesion frame 432 is formed on the top surface of the cushion-frame 454.Frame 432 extends beyond the edge of the cushion-frame 454 to contact thechip carrier 414 near the periphery thereof. The metal,lower adhesion frame 432 is preferably composed of Cr/Ni/Au adhesion layers or another suitable combination which can bond to thesolder preform 452 which is placed above thelower adhesion frame 432. - On the surface of the lower adhesion frame432 a
polymeric mask 451 has been formed and an opening has been formed above the top surface of the metallower adhesion frame 432 far away from the edge of the cushion-frame 454 to confinemolten solder 452 from thesolder preform 452 which has provides a hermetically sealed bond between the metallower adhesion frame 432 and the metalcover adhesion frame 442. Maskinglayer 451 prevents thesolder 452 from contacting the distal portions of thelower adhesion frame 432. Since themolten solder 452 may undercut thepolymeric mask 451, it is preferred that the gold portion of the metallower adhesion frame 432 should be plated to completeframe 432 only after the formation of thepolymeric mask 451. - The cover412 is positioned with the metal cover adhesion frame resting on the
solder preform 452. Then themodule 400 is heated above the melting point of thepreform 452 to provide a hermetically sealed bond between the metallower adhesion frame 432 and the metalcover adhesion frame 442. Thus the metalcover adhesion frame 442 on the bottom surfaces of thesides 427 of the cap 412 is bonded to the top surface of thesolder frame preform 452 and that provides full hermeticity. - In this case, there is no contact between
solder frame preform 452 and thechip carrier 414 as thelower adhesion frame 432 forms a floating via-seal 458 which extends across the tapered edge of the cushioning polymer cushion-frame 454 extending beyond the end of the edge of the body of the sealingstructure 431, to a distal location remote from thecover adhesion frame 442 and thesolder frame preform 452. Thus, the extension of the metallower adhesion frame 432 beyond the edge of thecushion frame 454 decouples thesolder frame preform 452 in the sealingstructure 431 from thechip carrier 414. - Modeling has shown a very significant reduction in stress transmitted to the chip carrier, compared to a solid solder frame. For a particular case, 55% reduction in cool down stress, and 76% reduction in thermal cycle stress. The thickness of the cushion-frame need be no greater than 12 micrometers to effect stress decoupling, and probably can be as thin as 5 micrometers.
- The x-y offset between the solder edge and the via-seal edge may be as little as 1 mm for effective stress coupling, and again, may be able to be even closer than that. This applies to all the embodiments.
- FIG. 5B shows a modification of the embodiment of FIG. 5A in which a
solder seal 431′is offset outboard from a metal/chip carrier contact via-seal 458′which is inside the cover 412. Note that thelayer 432′ reaches across the opposite end oflayer 454′. A metallower adhesion frame 432′ is formed on the top surface of the cushion-frame 454′so thatframe 432′ reaches down inside the cover 412 to contact thesurface 414T of thechip carrier 414. The cushion-frame 454′, the metallower adhesion frame 432′, and thepolymeric mask 451′are all reversed left to right. All of the elements of the module of FIG. 5B are otherwise the same as in FIG. SA. - FIG. 6 shows a simpler, “nearly hermetic” embodiment of the device of FIG. 2, which may be acceptable for many applications. Here the
ablated channel 55C of FIG. 3B and thechannel 155 of FIG. 2 are eliminated entirely. Hermeticity is slightly compromised only by the thinpolymeric cushion frame 554 which is preferably a polymer such as polyimide PI. - The
module 500 includes achip carrier 514 and a chip cover 512 fragments of which are shown bonded together and sealed by a sealingstructure 531 according to this invention. - The chip cover512 has a top 513 and four
vertical sides 527. Thesides 527 havevertical sidewalls 528 which are joined to thechip carrier 514 by ahermetic sealing structure 531. Thehermetic sealing structure 531 is formed between thesides 527 of cover 512 and thechip carrier 514, in accordance with this invention. A metalcover adhesion frame 542 is formed on the bottom of thevertical sides 527 of the cover 512. The metalcover adhesion frame 542 may be composed of layers comprising Ni—Au or another suitable combination, as described above. - The
chip carrier 514 supports aninterconnect structure 22 andchips 20 as described above. The soft, polymeric cushion-frame 554, as above, rests directly on the polished top surface of thechip carrier 514. A metallower adhesion frame 532 is formed on the top surface of the cushion-frame 554.Frame 532 does not contact thechip carrier 514. The metal,lower adhesion frame 532 is preferably composed of Cr/Ni/Au adhesion layers or another suitable combination. - On the surface of the lower adhesion frame532 a
solder preform 552 has been placed upon thelower adhesion frame 532. - Then the cover512 is positioned with the metal cover adhesion frame resting on the
solder preform 552. - Then the
module 500 is heated above the melting point of thepreform 552 to provide a hermetically sealed bond between the metallower adhesion frame 532 and the metalcover adhesion frame 442. - In this case there is no contact between
solder 552 and thechip carrier 514 and there is no floating via-seal but the metal-ceramic CTE (Coefficient of Thermal Expansion) stresses are isolated by the soft,non-metallic layer 554 which nearly provides a hermetic seal. - The
module 100 is tested for leaks with a helium (He) leak testing procedure at a rate of 5×10−7 cc/sec of He. - While this invention has been described in terms of the above specific embodiment(s), those skilled in the art will recognize that the invention can be practiced with modifications within the spirit and scope of the appended claims, i.e. that changes can be made in form and detail, without departing from the spirit and scope of the invention. Accordingly all such changes come within the purview of the present invention and the invention encompasses the subject matter of the claims which follow.
Claims (43)