US20030096547A1

US20030096547A1 - Elastic woven or knitted fabric, and cushioning material and seat using the same

Info

Publication number: US20030096547A1
Application number: US10/263,801
Authority: US
Inventors: Tetsushi Oka; Yasuo Ohta; Syouji Oda
Original assignee: Toyobo Co Ltd
Current assignee: Toyobo Co Ltd
Priority date: 2001-10-05
Filing date: 2002-10-04
Publication date: 2003-05-22
Also published as: ATE356235T1; DE60218593T2; EP1302578A2; EP1302578B1; EP1302578A3; DE60218593D1; EP1302578B8

Abstract

The present invention relates to an elastic woven or knitted fabric that has an elastic yarn comprising an organic synthetic macromolecule disposed in at least part thereof, and has the following physical properties:

(1) a stress at 10% elongation in a range of 100 to 600N per 5 cm width in at least one of a warp direction and a weft direction, and an elongation recovery factor at 15% elongation of at least 75% in the same direction;

(2) a ratio ST1/ST2 of not more than 5, wherein ST1 is the stress at 10% elongation in one of the warp and weft directions, and ST2 is the stress at 10% elongation in the other one of the warp and weft directions, with the proviso that ST1≧ST2; and

(3) a dry heat shrinkage factor at 180° C. in a range of 1.0% to 15% in each of the warp direction and the weft direction.

Description

FIELD OF THE INVENTION

The present invention relates to a woven or knitted fabric having excellent strength and elastic recoverability or a pleasant air permeability, and to a cushioning material, a chair-covering fabric and various types of seat using the woven or knitted fabric.

DESCRIPTION OF THE RELATED ART

Urethane foam, polyester fiber wadding, resin cotton or solid cotton having polyester fibers bonded thereto, and so on have conventionally been used as cushioning materials for furniture such as chairs, beds, seats for transportation machinery such as automobiles and trains, and so on. To obtain pleasant properties as a cushion, many materials used are devised in various ways, for example by combining materials having different cushioning abilities to one another, or by adopting a duplex structure when forming the cushion. However, all of these cushioning materials have had problems such as being bulky or it being impossible to obtain a material having a good cushioning ability with a small volume.

Moreover, the air permeability greatly influences the comfort when seated, but with conventional cushioning materials such as urethane foam, polyester fiber wadding, and resin cotton or hard cotton having polyester fibers bonded thereto, there has been a limit to how much the air permeability can be increased.

From these viewpoints, there are calls for the development of a material that has excellent cushioning ability with space-saving, or a material with added comfort.

It is an object of the present invention to provide an elastic woven or knitted fabric, in particular an elastic woven or knitted fabric for a seat that can be used as a cushioning material that has excellent cushioning ability and permanent set resistance, is space-saving, and has excellent air permeability.

SUMMARY OF THE INVENTION

The present invention provides the following.

1. An elastic woven or knitted fabric that has an elastic yarn comprising an organic synthetic macromolecule disposed in at least part thereof, and has the following physical properties:

(2) a ratio ST1/ST2 of not more than 5, where ST1 is the stress at 10% elongation in one of the warp and weft directions, and ST2 is the stress at 10% elongation in the other one of the warp and weft directions, with the proviso that ST1≧ST2; and

(3)a dry heat shrinkage factor at 180° C. in a range of 1.0% to 15% in each of the warp direction and the weft direction.

2. An elastic woven or knitted fabric that has an elastic yarn comprising an organic synthetic macromolecule disposed in at least part thereof, and has the following physical properties:

(1) a stress at 10% elongation in a range of 100 to 600N per 5 cm width, and an elongation recovery factor at 15% elongation of at least 75%, in at least one of a warp direction and a weft direction;

(2) an air permeability upon passing through air at a pressure of 125 Pa in a range of 100 to 700 cc/cm ²·sec; and

(3) a ratio ST1/ST2 of not more than 5, where ST1 is the stress at 10% elongation in one of the warp and weft directions, and ST2 is the stress at 10% elongation in the other one of the warp and weft directions, with the proviso that ST1≧ST2.

3. The elastic woven or knitted fabric according to 1 or 2 above, wherein the organic synthetic macromolecule is a polyester-based resin.

4. The elastic woven or knitted fabric according to 1 or 2 above, wherein the breaking strength is at least 250N per 5 cm width in each of the warp direction and the weft direction.

5. The elastic woven or knitted fabric according to 1 or 2 above, wherein the sliding resistance of the elastic yarn comprising the organic synthetic macromolecule is at least 2N.

6. The elastic woven or knitted fabric according to 1 or 2 above, wherein the elastic yarn comprising the organic synthetic macromolecule is a monofilament.

7. A method of manufacturing an elastic woven or knitted fabric, comprising the steps of:

carrying out knitting or weaving disposing in at least part an elastic yarn comprising at least two polyether-ester-based elastomers having different melting points to one another; and

then carrying out heat treatment at a temperature at which a low-melting-point polyether-ester-based elastomer component softens or melts;

whereby a woven or knitted fabric having the following physical properties is obtained:

(1) a stress at 10% elongation in a range of 100 to 600N per 5 cm width, and an elongation recovery factor at 15% elongation of at least 75%, in at least one of a warp direction and a weft direction; and

(2) a ratio ST1/ST2 of not more than 5, wherein ST1 is the stress at 10% elongation in one of the warp and weft directions, and ST2 is the stress at 10% elongation in the other one of the warp and weft directions, with the proviso that ST1≧ST2.

8. The method of manufacturing an elastic woven or knitted fabric according to 7 above, wherein a low-melting-point polyether-ester-based elastomer resin fuses and hardens through the heat treatment at parts of the woven or knitted fabric where the yarns intersect.

9. The method of manufacturing an elastic woven or knitted fabric according to 7 above, wherein the content in the woven or knitted fabric of the elastic yarn comprising the polyether-ester-based elastomers is at least 25 wt %.

10. The method of manufacturing an elastic woven or knitted fabric according to 7 above, wherein the elastic yarn comprising the polyether-ester-based elastomers has a core-sheath structure, and the melting point of a core component polyether-ester-based elastomer is at least 30° C. higher than the melting point of a sheath component polyether-ester-based elastomer.

11. The method of manufacturing an elastic woven or knitted fabric according to 10 above, wherein the weight ratio of the core component to the sheath component is in a range of 95:5 to 30:70.

12. A seat cushioning material that uses the elastic woven or knitted fabric according to 1 or 2 above.

13. A seat that uses the cushioning material according to 12 above.

The cushioning material here is a component used in any of various applications that utilize the cushioning properties thereof; there are no particular limitations on the method of using the cushioning material. For example, the cushioning material can be used in the seat and/or the back of an office chair, whereby the cushioning material alone gives a cushioning function, or the cushioning material can be used as part of a chair structure, combined, for example, with urethane foam, polyester fiber wadding, resin cotton or hard cotton having polyester fibers bonded thereto, or springs. Moreover, the cushioning material can be used combined with a separate designed fabric on the surface thereof.

Examples of specific applications of the elastic woven or knitted fabric and the cushioning material are office chairs, household chairs, seats for transportation machinery such as automobiles and trains, wheelchair seats, child seats, nursing chairs, bench seats, and folding chairs; however, the present invention is not limited to these.

There are no particular limitations on the raw materials of the elastic yarn comprising an organic synthetic macromolecule used in the present invention; nevertheless, the raw materials can by selected, for example, from ester-based resins, urethane-based resins, olefin-based resins, styrene-based resins, amide-based resins and so on; to obtain the strength, ability to recover after elongation and so on required of a woven or knitted fabric for seats, an aromatic polyester, for which an aromatic carboxylic acid and a glycol can be used as principal raw materials, is preferable. Furthermore, a polyester elastic yarn obtained by copolymerizing polybutylene terephthalate and polytetramethylene glycol is more preferable, since the ability to recover after elongation is good.

The elastic yarn comprising the organic synthetic macromolecule must be used in at least part of the woven or knitted fabric of the present invention in the warp and/or the weft direction. By using the elastic yarn, the ability to recover after elongation is kept good.

It is advantageous to use an elastic yarn comprising at least two polyether-ester-based elastomers having different melting points to one another as the elastic yarn in the present invention, since in this case, through carrying out heat treatment, a polyether-ester-based elastomer having a low melting point melts and resolidifies, whereby it becomes possible to carry out yarn fixing at points of intersection in the woven or knitted fabric, with the elastic modulus of a polyether-ester-based elastomer having a high melting point being maintained as is. Moreover, when the heat treatment has been carried out on the elastic yarn comprising polyether-ester-based elastomers having different melting points to one another, because the low-melting-point polyether-ester-based elastomer, which is flexible and has excellent elastic recoverability, fuses and solidifies at points of intersection between the warp and the weft in the case of a woven fabric or points of intersection between the yarns constituting the fabric in the case of a knitted fabric, strong yarn fixing can be obtained without there being a deterioration of the strength, elastic recovery factor and so on of the woven or knitted fabric.

The melting point of the low-melting-point polyether-ester-based elastomer is preferably at least 100° C. from the viewpoint of spinning ability and knitting/weaving ability, and is preferably at least 30° C. lower than the melting point of the high-melting-point polyether-ester-based elastomer from the viewpoint of the purpose of using the elastic yarn. Moreover, the ratio of usage of the high-melting-point polyether-ester-based elastomer to the low-melting-point polyether-ester-based elastomer can be chosen as deemed appropriate, but for practical reasons is preferably in a range of 95:5 to 30:70, more preferably in a range of 90:10 to 60:40, as a weight ratio. Furthermore, the heat treatment is preferably carried out at a temperature between a temperature 10° C. below the melting point of the high-melting-point elastic yarn and a temperature 10° C. above the melting point of the low-melting-point elastic yarn. By carrying out such heat treatment on the woven or knitted fabric, the elastic yarn can be sufficiently bonded to other yarns in contact therewith in the woven or knitted fabric. It goes without saying that the melting point of the polyester yarn used in the woven or knitted fabric must be at least as high as the melting point of the high-melting-point polyether-ester-based elastic yarn.

In the present invention, the elastic yarn can be used in either the warp direction or the weft direction of the woven or knitted fabric, but from the viewpoint of knitting/weaving ability and the product quality of the woven or knitted fabric, is preferably used in the weft direction. Moreover, the knit/weave can be selected from various knits/weaves such as warp knit (single raschel, double raschel, tricot), weft knit, plain weave, twill weave, satin weave, and leno weave, although the present invention is not limited to these.

It is particularly preferable for the elastic yarn in the present invention to be a monofilament yarn. There will be no problems with the mechanical properties such as the ability to recover after elongation even if the elastic yarn is a multifilament yarn, but the durability may be poor due to the resistance to friction being low. The fineness of the monofilament yarn is preferably between 100 dtex and 6000 dtex. At below 100 dtex, the resistance to friction will be low and it may not being possible to obtain sufficient durability, whereas at above 6000 dtex, handling during manufacture of the woven or knitted fabric will become difficult. A more preferable range for the fineness is from 300 dtex to 3000 dtex. Moreover, a multifilament yarn with single filaments of fineness at least 100 dtex can be used.

A polyester yarn, a polyamide yarn, a polyolefin yarn or the like can be used together with the elastic yarn as the yarn other than the elastic yarn in the present invention, and regarding these yarns, an unprocessed yarn may be used, or a processed yarn such as a loop yarn or a false twist yarn may be used, or both may be used mixed together. Moreover, the yarn used can be a spun-dyed yarn or a fiber-dyed yarn. In the case that a polyester-based elastomer yarn is used as the elastic yarn, and a polyester yarn is used as the yarn used together with the elastic yarn, the yarns constituting the woven or knitted fabric all become polyester-based, which is preferable in that recycling becomes easy.

The sliding resistance of the elastic yarn comprising the organic synthetic macromolecule in the woven or knitted fabric of the present invention is an important physical property as a seat cushioning material. It is preferable for the value thereof to be at least 2N. If the sliding resistance is less than 2N, then yarn slippage and fraying will occur, which is undesirable. The sliding resistance is more preferably at least 5N, yet more preferably at least 10N.

The breaking strength in each of the warp direction and the weft direction of the woven or knitted fabric of the present invention is also an important physical property as a seat cushioning material. It is preferable for the value thereof to be at least 250N per 5 cm width. If the breaking strength is less than 250N per 5 cm width, then the woven or knitted fabric may break through the load to which the surface is subjected during use as a cushioning material, which is undesirable. The breaking strength is more preferably at least 350N per 5 cm width.

The stress at 10% elongation in at least one of the warp direction and the weft direction of the woven or knitted fabric of the present invention is in a range of 100 to 600N per 5 cm width, preferably in a range of 150 to 400N per 5 cm width. At less than 100N per 5 cm width, the sinking amount during use as a cushioning material will be large, and during use as a seat in particular there will be discomfort when seated. On the other hand, at above 600N per 5 cm width, the sinking amount when used as a seat will be too low, and hence aching will arise while seated, and thus it will not be possible to tolerate prolonged usage.

Moreover, the elongation recovery factor after 15% elongation in the same direction as above is at least 75%, preferably at least 80%. The elongation recovery factor here is measured as follows. A strip of width 5 cm is cut out from the woven or knitted fabric, and using a constant extension rate type testing machine, the sample is elongated by 15% with a gripping interval of 20 cm and a pulling rate of 20 cm/min, then the load is released rapidly, and then once the sample has returned to its original length, the sample is once again elongated rapidly. The gripping interval when the stress rises during this second elongation is read, and the elongation recovery factor is calculated from the following formula.

((L2−L1)/(L1×0.15))×100(%)

Here, L1 is the initial gripping interval (=20 cm), and L2 is the gripping interval when the stress rises during the second elongation.

If the elongation recovery factor determined in this way is less than 75%, then wrinkles will arise during use as a cushioning material, which is unsuitable from the perspective of the external appearance and the feeling when seated.

Moreover, it is important that the dry heat shrinkage factor at 180° C. be in a range of 1.0% to 15% in each of the warp direction and the weft direction of the woven or knitted fabric. When the elastic woven or knitted fabric of the present invention is made into a product, wrinkles can be removed through heat treatment by utilizing the shrinkage properties, and if the dry heat shrinkage factor is less than 1.0% then it will not be possible to remove wrinkles sufficiently when making into a product as a cushioning material. Moreover, if the dry heat shrinkage factor is greater than 15%, then the dimensional stability will be poor, leading to problems in handling in subsequent manufacturing steps. The dry heat shrinkage factor is preferably in a range of 2.0 to 10%.

Moreover, the air permeability when passing air through a sample of the woven or knitted fabric of the present invention at a pressure of 125 Pa must be in a range of 100 to 700 cc/cm ²·sec. When used as a cushioning material, if the air permeability is less than 100 cc/cm²·sec, then a feeling of stickiness will be prone to arising upon sitting for a prolonged time, and moreover once the cushioning material has become damp it will not dry easily, and hence there will be a problem from the perspective of hygiene. On the other hand, if the air permeability is greater than 700 cc/cm²·sec, then the flow of air will be prone to becoming too great, and hence there will be a problem from the perspective of warmth retention. A more preferable range for the air permeability is 150 to 400 cc/cm²·sec.

Moreover, the ratio ST1/ST2 is preferably not more than 5, more preferably not more than 3, wherein ST1 is the stress at 10% elongation in one of the warp and weft directions, and ST2 is the stress at 10% elongation in the other one of the warp and weft directions, with the proviso that ST1≧ST2.

This is because if ST1/ST2 is greater than 5, then one of the warp yarn and the weft yarn will be subjected to an excessive load, and hence permanent set in fatigue will arise in the yarn subjected to the excessive load, and thus there will be a large drop in performance.

If it is necessary to make the woven or knitted fabric of the present invention fire-retardant and light-resistant, then yarns containing a fire retardant and a light resistance agent can be used, or else a fire retardant and a light resistance agent can be applied to the woven or knitted fabric. With regard to making the elastic yarn fire-retardant, known methods include mixing melamine cyanurate into the raw material resin, and applying a phosphorus compound, but there is no particular limitation to these. Moreover, regarding a light resistance agent, light resistance treatment can be carried out by adding carbon black or the like, but there is no particular limitation to this.

If it is necessary to make the elastic yarn used in the woven or knitted fabric of the present invention colored or mat, then dyes, pigments, inorganic particles and so on may be included. Regarding pigments and inorganic particles, a phthalocyanine-based organic pigment, carbon black, titanium oxide, silica, zinc oxide and so on can be added, but there is no particular limitation to these. By using a spun-dyed yarn containing a pigment, the effort of dying at a later stage can be dispensed with.

Next, a description will be given of an example of the manufacture of the woven or knitted fabric of the present invention. To obtain a novel woven or knitted fabric in this way, it is recommended that manufacturing be carried out carefully under optimum conditions.

In the present invention, heat treatment is carried out as means for fixing together the yarns at points of intersection in the woven or knitted fabric, and by optimizing the conditions of the heat treatment, the shrinkage factor of the product can be controlled. There are no particular limitations on the equipment used for carrying out the heat treatment, provided the equipment is such that the woven or knitted fabric can be heated while constraining shrinkage in the warp and weft directions by some method; nevertheless, it is preferable to use equipment such that both edges of the woven or knitted fabric can be fastened using pins or clips. During the heat treatment, to control the shrinkage factor in the warp direction of the woven or knitted fabric, it is important to set the overfeed factor to the optimum value. The overfeed factor must be set in accordance with the shrinkage factor in the warp direction in the case of heating the woven or knitted fabric in an unconstrained state, and it is particularly preferable to make the overfeed factor be in the following range.

1.5≦((SH1)−(overfeed factor))≦15

Here, SH1 represents the dry heat shrinkage factor at 180° C. in the warp direction when the woven or knitted fabric is unconstrained. The overfeed factor is calculated using the following formula from the feeding rate at the inlet part of the heat treatment equipment and the take-up rate at the take-up part of the heat treatment equipment for when the woven or knitted fabric is put into the heat treatment equipment.

Overfeed factor=100×(V1−V2)/V1

Here, V1 represents the feeding rate at the inlet part of the heat treatment equipment, and V2 represents the take-up rate at the take-up part of the heat treatment equipment.

Moreover, it is necessary to control the width variation factor in the weft direction of the woven fabric. The width variation factor must be set in accordance with the shrinkage factor in the weft direction in the case of heating the woven or knitted fabric in an unconstrained state, and is made to be in the following range.

1.5≦((SH2)−(width variation factor))≦15

Here, SH2 represents the dry heat shrinkage factor at 180° C. in the weft direction when the woven or knitted fabric is unconstrained.

The width variation factor is calculated using the following formula from the width between the fixed edges at the inlet part of the heat treatment equipment and the width between the fixed edges at the outlet part of the heat treatment equipment for when the woven or knitted fabric is put into the heat treatment equipment.

Width variation factor=100×(W1−W2)/W1

Here, W1 represents the width between the fixed edges at the inlet part of the heat treatment equipment, and W2 represents the width between the fixed edges at the outlet part of the heat treatment equipment.

Office chairs, automobile seats, train seats, nursing chairs, child seats, wheelchairs, folding chairs and bench seats that use the elastic woven or knitted fabric according to the present invention as a cushioning material have various advantages, for example the air permeability is excellent, weight reduction is possible, and the thickness can be reduced and hence the chair or seat can be made compact, and thus novel design is possible.

BEST MODE FOR CARRYING OUT THE INVENTION

Following is a description of the present invention through examples. However, the present invention is not limited by these examples. The measurement methods used in the examples are as follows.

Strength and Elongation for Raw Yarn

Measurements were carried out in accordance with JIS L 1013 using a constant extension rate type testing machine with a gripping interval of 100 mm and a pulling rate of 100 mm/min.

Shrinkage Factor for Raw Yarn

The raw yarn was put into a drying oven at 180° C. in an unconstrained state and dry heat treatment was carried out for 30 minutes, and then the shrinkage factor was calculated using the following formula.

((L1−L2)/(L1))×100(%)

Here, L1 is the length of the sample before the heat treatment (=30 cm), and L2 is the length of the sample after the heat treatment.

Strength and Elongation for Woven Fabric and Stress at 10% Elongation

Measurements were carried out in accordance with JIS L 1096 using a constant extension rate type testing machine with a gripping interval of 200 mm, a test piece width of 50 mm, and a pulling rate of 100 mm/min.

Elongation Recovery Factor

A strip of width 5 cm is cut out from the woven or knitted fabric, and using a constant extension rate type testing machine, the sample is elongated by 15% with a gripping interval of 20 cm and a pulling rate of 20 cm/min, then the load is released rapidly, and then once the sample has returned to its original length, the sample is once again elongated rapidly. The gripping interval when the stress rises during this second elongation is read, and the elongation recovery factor is calculated from the following formula.

((L4−L3)/(L3×0.15))×100(%)

Here, L3 is the initial gripping interval (=20 cm), and L4 is the gripping interval when the stress rises during the second elongation.

Dry Heat Shrinkage Factor

Strips of width 1 cm and length 20 cm are cut out from the woven or knitted fabric in each of the warp direction and the weft direction, the strips are put into a drying oven at 180° C. and dry heat treatment is carried out for 30 minutes, and then the dry heat shrinkage factor is calculated from the following formula.

((L5−L6)/(L5))×100(%)

Here, L5 is the length of the sample before the heat treatment (=20 cm), and L6 is the length of the sample after the heat treatment.

Sitting Performance

The woven or knitted fabric was fastened in a horizontal plane into a 40 cm-square iron frame, a 65 kg load was applied to the center of the woven or knitted fabric using a loading plate having a bottom face of diameter 20 cm, and the sinking amount of the loading plate relative to the horizontal plane before the application of the load was measured.

Ten monitors were asked to sit on a model chair made by fastening the woven or knitted fabric into a 40 cm-square frame, and judge the feeling. Each person evaluated the comfort when seated as described below, and overall judgement was carried out by taking the average of the evaluation results.

[Evaluation] Comfort when seated is good: A; comfort when seated is normal: B; comfort when seated is poor: D.

Moreover, the seat of the model chair was visually observed immediately after the evaluation of the comfort when seated, and the recovery from wrinkles was judged as described below. As with the comfort when seated, overall judgement was carried out by taking the average of the judgement results for the ten people.

[Evaluation] No wrinkles: A; slight wrinkles: B; wrinkles clearly remain: D

Fraying=Yarn Fixing Ability

The sliding resistance was measured by the yarn extraction method A in accordance with JIS L 1096. The measurements were carried out using a constant extension rate type testing machine with a gripping interval of 30 mm, a test piece width of 20 mm, and a pulling rate of 30 mm/min.

Air Permeability

The amount of air passing through the test piece when the differential pressure was 125 Pa was measured using a fragile type testing machine in accordance with JIS L 1096 (air permeability, A method, fragile type method).

Feeling of Stickiness

Ten monitors were asked to sit on a model chair made by fastening the sample into a 40 cm-square frame, and judge the feeling of stickiness. The feeling of stickiness was judged as described below after sitting for 1 hour in a room at 28° C. and 75% RH, and overall judgement was carried out by taking the average of the judgement results.

[Evaluation] Pleasant, with no feeling of stickiness: A; no feeling of stickiness, but lack of warmth retention: B; stickiness felt: C.

EXAMPLE 1A

A woven fabric of plain weave was produced using a 2080 dtex elastic yarn at a density of 20 yarns per inch as the weft, and a 830 dtex polyester multifilament yarn at a density of 28 yarns per inch as the warp; the elastic yarn had a polyether-ester-based elastomer of melting point 222° C. as a core component, and a polyether-ester-based elastomer of melting point 182° C. as a sheath component, with the weight ratio of the core to the sheath being 80:20. The dry heat shrinkage factor of the woven fabric upon heating in an unconstrained state was 8.0% in the warp direction and 15% in the weft direction. The woven fabric was thus subjected to dry heat treatment at 200° C. for 1 minute with the overfeed factor being set to 3.0% and the width variation factor being set to 13%. [0088]
It was verified that in the woven fabric after the heat treatment the low-melting-point polyether-ester-based elastomer had bonded and solidified at parts where the warp and the weft intersect in the woven fabric. [0089]
Moreover, the dry heat shrinkage factor of the woven fabric was measured after carrying out the heat treatment, and was found to be 5.0% in the warp direction and 2.0% in the weft direction. The woven fabric was fastened into a 40 cm×40 cm frame, and heat setting was carried out in this state at 195° C. The cushioning material thus obtained had no wrinkles and had excellent dimensional stability. [0090]
Moreover, an office chair was manufactured using the cushioning material, whereupon the feeling when seated was extremely good, and there were no wrinkles after sitting; the cushioning material could thus be satisfactorily used as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 1. [0091]

EXAMPLE 2A

Testing was carried out as in Example 1A, except that the weave of the woven fabric was made to be a 2/1 twill weave. The dry heat shrinkage factor when the woven fabric was heated in an unconstrained state before carrying out heat treatment was 8.2% in the warp direction and 15.2% in the weft direction. The dry heat shrinkage factor of the woven fabric after carrying out the heat treatment was 5.2% in the warp direction and 2.2% in the weft direction. The woven fabric was fastened into a 40 cm×40 cm frame, and heat setting was carried out in this state at 195° C. The cushioning material thus obtained had no wrinkles and had excellent dimensional stability. [0092]
Moreover, an office chair was manufactured using the cushioning material, whereupon the feeling when seated was extremely good, and there were no wrinkles after sitting; the cushioning material could thus be satisfactorily used as a seat cushioning material for office chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 1. [0093]

EXAMPLE 3A

Testing was carried out as in Example 2A, except that the density of the warp in the woven fabric was made to be 36 yarns per inch and the density of the weft was made to be 15 yarns per inch. The dry heat shrinkage factor when the woven fabric was heated in an unconstrained state before carrying out heat treatment was 8.3% in the warp direction and 15.3% in the weft direction. The dry heat shrinkage factor of the woven fabric after carrying out the heat treatment was measured to be 5.3% in the warp direction and 2.3% in the weft direction. The woven fabric was fastened into a 40 cm×40 cm frame, and heat setting was carried out in this state at 195° C. The cushioning material thus obtained had no wrinkles and had excellent dimensional stability. [0094]
Moreover, an office chair was manufactured using the cushioning material, whereupon the feeling when seated was extremely good, and there were no wrinkles after sitting; the cushioning material could thus be satisfactorily used as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 1. [0095]

EXAMPLE 4A

Chairs were manufactured by using the woven fabrics of Examples 1A to 3A as seats, and integrally molding with a polyester resin seat frame and backrest using an approximately quadrangular mold surrounded on all four sides. The chairs manufactured were light and easily carried. Moreover, comparing with a conventional chair in which urethane is used for both the seat and the back, it was found that due to the lack of thickness, sufficient seating space could be obtained even in a cramped indoor environment. Furthermore, the feeling when seated was extremely pleasant, with there being a suitable degree of sinking, and with there being no feeling of stickiness even during use in a high-temperature, high-humidity environment; it was found that the elastic woven fabrics according to the present invention have an excellent performance as a chair-covering fabric or a cushioning material, and moreover that seats using these elastic woven fabrics can be used with office chairs or seats for transportation machinery such as automobiles and trains. [0096]

COMPARATIVE EXAMPLE 1A

A plain woven fabric was produced using 830 dtex polyester at a density of 28 yarns per inch as both the warp and the weft, and testing was carried out as in Example 1A. The dry heat shrinkage factor when the woven fabric was heated in an unconstrained state before carrying out heat treatment was 8.5% in the warp direction and 8.5% in the weft direction, and during the heat treatment the overfeed factor was made to be 2.5% and the width variation factor was made to be 2.5%. The dry heat shrinkage factor of the woven fabric after carrying out the heat treatment was measured to be 6.0% in the warp direction and 6.0% in the weft direction. The woven fabric was fastened into a 40 cm×40 cm frame, and heat setting was carried out in this state at 195° C. The cushioning material thus obtained had no wrinkles and had excellent dimensional stability. [0097]
However, when an office chair was manufactured using this cushioning material, regarding the sitting performance, the feeling was extremely poor, possibly because the sinking amount was extremely low, and moreover there were wrinkles in the fabric after sitting; the cushioning material was thus unsuitable as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 1. [0098]

COMPARATIVE EXAMPLE 2A

Testing was carried out as in Example 1A, except that during the heat treatment after producing the woven fabric, the overfeed factor was made to be 7.0% and the width variation factor was made to be 14.2%. The dry heat shrinkage factor of the woven fabric after carrying out the heat treatment was measured to be 1.0% in the warp direction and 0.8% in the weft direction. The woven fabric was fastened into a 40 cm×40 cm frame, and heat setting was carried out in this state at 195° C. However, wrinkles remained in the cushioning material obtained. Moreover, when an office chair was manufactured using the cushioning material, it was found that the level was not sufficient for use as a cushioning material from the viewpoint of the external appearance product quality due to wrinkles clearly remaining. [0099]

COMPARATIVE EXAMPLE 3A

Testing was carried out as in Example 1A, but using a high shrinkage type elastic yarn as the weft, and a high shrinkage type polyester multifilament yarn as the warp. The dry heat shrinkage factor of the woven fabric in an unconstrained state before carrying out the heat treatment was 25% in the warp direction and 32% in the weft direction. Moreover, the conditions during the heat treatment were made to be an overfeed factor of 7.0% and a width variation factor of 15%. The dry heat shrinkage factor of the woven fabric after carrying out the heat treatment was measured to be 18% in the warp direction and 17% in the weft direction. The woven fabric was fastened into a 40 cm×40 cm frame, and heat setting was carried out in this state at 195° C. Wrinkles did not remain in the cushioning material obtained, but because the shrinkage factor was too high, the dimensions of the product could not be controlled, and hence it was found that the level was not sufficient for use as a cushioning material. [0100]

COMPARATIVE EXAMPLE 4A

Testing was carried out as in Example 1A, except that the density of the warp in the woven fabric was made to be 32 yarns per inch and the density of the weft was made to be 10 yarns per inch. The dry heat shrinkage factor when the woven fabric was heated in an unconstrained state before carrying out heat treatment was 8.0% in the warp direction and 15% in the weft direction. [0101]
Moreover, the dry heat shrinkage factor of the woven fabric after carrying out the heat treatment was measured to be 5.0% in the warp direction and 2.0% in the weft direction. The woven fabric was fastened into a 40 cm×40 cm frame, and heat setting was carried out in this state at 195° C. The cushioning material thus obtained had no wrinkles and had excellent dimensional stability. [0102]
However, when an office chair was manufactured using the cushioning material, the feeling was normal, possibly because the sinking amount during sitting was somewhat high, but wrinkles clearly remained after sitting. The cushioning material was thus unsuitable as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 1. [0103]
The following were found from the results for the examples and the comparative examples. The woven fabric in each of Examples 1A to 3A was a woven fabric that uses an elastic yarn comprising two polyether-ester-based elastomers having different melting points to one another as the weft and a polyester yarn as the warp, and for which yarn fixing was carried out by carrying out dry heat treatment, and was designed such that the stress at 10% elongation is in a range of 100 to 600N per 5 cm width in at least one of the warp direction and the weft direction and the elongation recovery factor at 15% elongation is at least 75% in the same direction, the dry heat shrinkage factor of the woven fabric at 180° C. is in a range of 1.0% to 15% in both the warp direction and the weft direction, and ST1/ST2 is not more than 5. These fabrics used in the examples had a suitable hardness and sinking amount, and the elongation recoverability was satisfactory. Moreover, there was sliding resistance, there was no fraying or yarn slippage, and the feeling when seated was excellent, and hence these woven fabrics satisfied all of the properties required of a cushioning material. [0104]
With Comparative Example 1A, a polyester yarn was used as both the warp and the weft, and hence the stress at 10% elongation exceeded 600N per 5 cm width in both the warp direction and the weft direction. The sinking amount for this fabric was extremely low, and hence the feeling was extremely poor. Moreover, wrinkles arose while sitting, and hence it was found that the fabric is unsuitable as a cushioning material. [0105]
With Comparative Example 2A, the dry heat shrinkage factor of the woven fabric at 180° C. was less than 1.0%, and hence when producing the product, wrinkles could not be sufficiently removed even when heat treatment was carried out as a final manufacturing step; it was thus found that the fabric was unsuitable as a cushioning material from the viewpoint of external appearance product quality. [0106]
With Comparative Example 3A, the dry heat shrinkage factor of the woven fabric at 180° C. was greater than 15%, and hence when producing the product, the shrinkage factor was too high upon carrying out heat treatment as a final manufacturing step, and thus the product dimensions could not be controlled; it was thus found that the fabric was unsuitable as a cushioning material. [0107]

As with the examples, the woven fabric of Comparative Example 4A was a woven fabric that uses an elastic yarn comprising two polyether-ester-based elastomers having different melting points to one another as the weft and a polyester yarn as the warp, and for which yarn fixing was carried out by carrying out dry heat treatment, but was designed such that ST1/ST2 was greater than 5. The sinking amount for this fabric was somewhat high, and the comfort when seated was normal. However, wrinkles arose while sitting, and hence it was found that the fabric was unsuitable as a cushioning material.

TABLE 1


Example	Example	Example	Comparative	Comparative	Comparative	Comparative
1A	2A	3A	Example 1A	Example 2A	Example 3A	Example 4A

Warp
Type	Polyester	Polyester	Polyester	Polyester	Polyester	Polyester	Polyester
	yarn	yarn	yarn	yarn	yarn	yarn	yarn
Fineness	830	830	830	830	830	830	830
(dtex)
Number of	96	96	96	96	96	96	96
filaments
Strength	7.5	7.5	7.5	7.5	7.5	7.3	7.5
(cN/dtex)
Elongation	20	20	20	20	20	18	20
(%)
Shrinkage	8.6	8.6	8.6	8.6	8.6	25	8.6
factor (%)
Weft
Type	Polyether-	Polyether-	Polyether-	Polyester	Polyether-	Polyether-	Polyether-
	ester-based	ester-based	ester-based	yarn	ester-based	ester-based	ester-based
	elastic yarn	elastic yarn	elastic yarn		elastic yarn	elastic yarn	elastic yarn
Composite	Core-sheath	Core-sheath	Core-sheath	None	Core-sheath	Core-sheath	Core-sheath
structure	(80:20)	(80:20)	(80:20)		(80:20)	(80:20)	(80:20)
Fineness	2080	2080	2080	830	2080	2080	2080
(dtex)
Number of	1	1	1	96	1	1	1
filaments
Strength	2.1	2.1	2.1	7.5	2.1	2.1	2.1
(cN/dtex)
Elongation	120	120	120	20	120	120	120
(%)
Woven fabric
Weave	Plain	2/1 twill	2/1 twill	Plain	Plain	Plain	Plain
Warp
direction
Density (yarns	28	28	36	28	28	28	32
per inch)
Tensile strength	3020	3060	3890	3040	3010	3080	3420
(N/5 cm)
Tensile elongation	40	43	42	40	40	40	40
(%)
Stress at 10%	760	760	970	760	760	760	870
elongation (N
per 5 cm
width)
Elongation recovery	65	63	64	65	65	65	64
factor (%)
Shrinkage factor after	5.0	5.2	5.3	6.0	1.0	18	5.1
heat treatment (%)
Weft direction
Density (yarns	20	20	15	28	20	20	10
per inch)
Tensile strength	1200	1200	930	3020	1200	1200	620
(N/5 cm)
Tensile elongation	135	138	139	40	135	135	135
(%)
Stress at 10%	300	300	230	760	300	300	150
elongation (N per
5 cm width)
Elongation recovery	85	84	85	65	85	85	84
factor (%)
Shrinkage factor after	2.0	2.2	2.3	6.0	0.8	17	2.0
heat treatment (%)
ST1/ST2	2.5	2.5	4.2	1.0	2.5	2.5	5.8
Sliding resistance (N)	41	26	31	0.6	36	41	52
Sitting
Sinking amount	30	31	27	16	32		40
(mm)
Feeling	A	A	A	D	A		B
Recovery from	A	A	A	D	D		D
wrinkles

EXAMPLE 1B

A woven fabric of plain weave was produced using a 2080 dtex elastic yarn at a density of 20 yarns per inch as the weft, and a 830 dtex polyester multifilament yarn at a density of 28 yarns per inch as the warp; the elastic yarn had a polyether-ester-based elastomer of melting point 222° C. as a core component, and a polyether-ester-based elastomer of melting point 182° C. as a sheath component, with the weight ratio of the core to the sheath being 80:20. Dry heat treatment was carried out on the woven fabric at 200° C. for 1 minute. [0109]
It was verified that in the woven fabric after the heat treatment the low-melting-point polyether-ester-based elastomer had bonded and solidified at parts where the warp and the weft intersect in the woven fabric. [0110]
Moreover, the feeling when seated for the sample after the heat treatment was extremely good, and there were no wrinkles after sitting; the sample could thus be satisfactorily used as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 2. [0111]

EXAMPLE 2B

Testing was carried out as in Example 1B, except that the weave of the woven fabric was made to be a 2/1 twill weave. The feeling when seated for the sample after the heat treatment was extremely good, and there were no wrinkles after sitting; the sample could thus be satisfactorily used as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 2. [0112]

EXAMPLE 3B

Testing was carried out as in Example 2B, except that the density of the warp in the woven fabric was made to be 36 yarns per inch and the density of the weft was made to be 15 yarns per inch. The feeling when seated for the sample after the heat treatment was extremely good, and there were no wrinkles after sitting; the sample could thus be satisfactorily used as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 2. [0113]

COMPARATIVE EXAMPLE 1B

Testing was carried out as in Example 1B, except that the density of the warp in the woven fabric was made to be 32 yarns per inch and the density of the weft was made to be 10 yarns per inch. For the sample after the heat treatment, the feeling was normal, possibly because the sinking amount during sitting was somewhat high, but wrinkles clearly remained after sitting. The sample was thus unsuitable as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 2. [0114]

COMPARATIVE EXAMPLE 2B

A plain woven fabric was produced using 830 dtex polyester at a density of 28 yarns per inch as both the warp and the weft, and testing was carried out as in Example 1B. The feeling when seated was extremely poor, possibly because the sinking amount was extremely low, and moreover there were wrinkles in the fabric after sitting; the fabric was thus unsuitable as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 2. [0115]

COMPARATIVE EXAMPLE 3B

Testing was carried out as in Example 1B, except that the density of the warp in the woven fabric was made to be 15 yarns per inch and the density of the weft was made to be 12 yarns per inch. The feeling of the sample after the heat treatment was normal, possibly because the sinking amount during sitting was somewhat high, and there was sufficient recovery from wrinkles after sitting. However, even though the feeling was good, the air permeability was extremely high, which was not pleasant from the perspective of warmth retention. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 2. [0116]

COMPARATIVE EXAMPLE 4B

Using a cushioning material comprising commercially sold urethane foam of thickness 50 mm and density 60 kg/m[0117] ³, evaluation was carried out of the sitting performance, the air permeability, and the feeling of stickiness. The feeling when seated and the recovery from wrinkles were good, but a feeling of stickiness arose during prolonged usage, which was unpleasant.
The following were found from the results for the examples and the comparative examples. The woven fabric in each of Examples 1B to 3B was a woven fabric that uses an elastic yarn comprising two polyether-ester-based elastomers having different melting points to one another as the weft and a polyester yarn as the warp, and for which yarn fixing was carried out by carrying out dry heat treatment, and was designed such that ST1/ST2 is not more than 5. These fabrics used in the examples had a suitable hardness and sinking amount, and the elongation recoverability was satisfactory. Moreover, there was sliding resistance, there was no fraying or yarn slippage, and the feeling when seated was excellent, and hence these woven fabrics satisfied all of the properties required of a cushioning material. [0118]
As with the examples, the woven fabric of Comparative Example 1B was a woven fabric that uses an elastic yarn comprising two polyether-ester-based elastomers having different melting points to one another as the weft and a polyester yarn as the warp, and for which yarn fixing was carried out by carrying out dry heat treatment, but was designed such that ST1/ST2 was greater than 5. The sinking amount for this fabric was somewhat high, and the feeling was not necessarily good. Moreover, wrinkles arose while sitting, and hence it was found that the fabric was unsuitable as a cushioning material. [0119]
With Comparative Example 2B, a polyester yarn was used as both the warp and the weft, and hence the stress at 10% elongation exceeded 600N per 5 cm width in both the warp direction and the weft direction. The sinking amount for this fabric was extremely low, and hence the feeling was extremely poor. Moreover, wrinkles arose while sitting, and hence it was found that the fabric is unsuitable as a cushioning material. [0120]
As with the examples, the woven fabric of Comparative Example 3B was a woven fabric that uses an elastic yarn comprising two polyether-ester-based elastomers having different melting points to one another as the weft and a polyester yarn as the warp, and for which yarn fixing was carried out by carrying out dry heat treatment, but the air permeability was extremely high, possibly due to the weave density being extremely coarse, which was not pleasant from the perspective of warmth retention after sitting for a prolonged time. [0121]

For Comparative Example 4B, the cushioning material comprised commercially sold urethane foam; the general sitting performance was satisfactory, but the air permeability was extremely low, and hence a feeling of stickiness arose upon sitting for a prolonged time, which was unpleasant.

TABLE 2


Example	Example	Example	Comparative	Comparative	Comparative	Comparative
1B	2B	3B	Example 1B	Example 2B	Example 3B	Example 4B

Warp
Type	Polyester	Polyester	Polyester	Polyester	Polyester	Polyester
	yarn	yarn	yarn	yarn	yarn	yarn
Fineness	830	830	830	830	830	830
(dtex)
Number of	96	96	96	96	96	96
filaments
Strength	7.5	7.5	7.5	7.5	7.5	7.5
(cN/dtex)
Elongation	20	20	20	20	20	20
(%)
Weft
Type	Polyether-	Polyether-	Polyether-	Polyester	Polyether-	Polyether-
	ester-based	ester-based	ester-based	ester-based	yarn	ester-based
	elastic yarn	elastic yarn	elastic yarn	elastic yarn		elastic yarn
Composite	Core-sheath	Core-sheath	Core-sheath	Core-sheath	None	None
structure	(80:20)	(80:20)	(80:20)	(80:20)
Fineness	2080	2080	2080	2080	830	2080
(dtex)
Number of	1	1	1	1	96	1
filaments
Strength	2.1	2.1	2.1	2.1	7.5	2.1
(cN/dtex)
Elongation	120	120	120	120	20	1
(%)
Woven fabric
Weave	Plain	2/1 twill	2/1 twill	Plain	Plain	Plain
Warp
direction
Density (yarns	28	28	36	32	28	15
per inch)
Tensile strength	3020	3010	3810	3400	3060	1640
(N/5 cm)
Tensile elongation	40	43	42	40	40	40
(%)
Stress at 10%	760	760	970	870	760	410
elongation (N
per 5 cm
width)
Elongation recovery	65	63	64	64	65	65
factor (%)
Weft direction
Density (yarns	20	20	15	10	28	12
per inch)
Tensile strength	1200	1200	930	620	3050	700
(N/5 cm)
Tensile elongation	135	138	139	135	40	137
(%)
Stress at 10%	300	300	220	150	760	190
elongation (N per
5 cm width)
Elongation recovery	85	84	85	84	65	84
factor (%)
ST1/ST2	2.5	2.5	4.4	5.8	1.0	2.2
Sliding resistance (N)	41	26	21	36	0.6	20
Sitting
performance
Sinking amount	30	31	34	40	21	46	40
(mm)
Feeling	A	A	A	B	D	B	B
Recovery from	A	A	A	D	D		D
wrinkles	A	A	A	D	D	A	A
Air
permeability
Air permeability	272	243	226	342	60	850	20
(cc/cm²· sec)
Feeling of stickiness	A	A	A	A	A	B	C

EXAMPLE 1C

A woven fabric of plain weave was produced using a 2080 dtex elastic yarn at a density of 20 yarns per inch as the weft, and a 830 dtex polyester multifilament yarn at a density of 28 yarns per inch as the warp; the elastic yarn had a polyether-ester-based elastomer of melting point 222° C. as a core component, and a polyether-ester-based elastomer of melting point 182° C. as a sheath component, with the weight ratio of the core to the sheath being 80:20. Dry heat treatment was carried out on the woven fabric at 200° C. for 1 minute. [0123]
It was verified that in the woven fabric after the heat treatment the low-melting-point polyether-ester-based elastomer had bonded and solidified at parts where the warp and the weft intersect in the woven fabric. [0124]
Moreover, the feeling when seated for the sample after the heat treatment was extremely good, and there were no wrinkles after sitting; the sample could thus be satisfactorily used as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 3. [0125]

EXAMPLE 2C

Testing was carried out as in Example 1C, except that the weave of the woven fabric was made to be a 2/1 twill weave. The feeling when seated for the sample after the heat treatment was extremely good, and there were no wrinkles after sitting; the sample could thus be satisfactorily used as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 3. [0126]

EXAMPLE 3C

Testing was carried out as in Example 2C, except that the density of the warp in the woven fabric was made to be 36 yarns per inch and the density of the weft was made to be 15 yarns per inch. The feeling when seated for the sample after the heat treatment was extremely good, and there were no wrinkles after sitting; the sample could thus be satisfactorily used as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 3. [0127]

EXAMPLE 4C

Chairs were manufactured by using the woven fabrics of Examples 1C to 3C as seats, and integrally molding with a polyester resin seat frame and backrest using an approximately quadrangular mold surrounded on all four sides. The chairs manufactured were light and easily carried. Moreover, comparing with a conventional chair in which urethane is used for both the seat and the back, it was found that due to the lack of thickness, sufficient seating space could be obtained even in a cramped indoor environment. Furthermore, the feeling when seated was extremely pleasant, with there being a suitable degree of sinking, and with there being no feeling of stickiness even during use in a high-temperature, high-humidity environment; it was found that the elastic woven fabrics according to the present invention have an excellent performance as a chair-covering fabric or a cushioning material, and moreover that seats using these elastic woven fabrics can be used with office chairs, household chairs, seats for transportation machinery such as automobiles and trains, wheelchair seats, child seats, nursing chairs, bench seats, folding chairs, and so on. [0128]

COMPARATIVE EXAMPLE 1C

Testing was carried out as in Example 1C, except that the density of the warp in the woven fabric was made to be 32 yarns per inch and the density of the weft was made to be 10 yarns per inch. For the sample after the heat treatment, the feeling was normal, possibly because the sinking amount during sitting was somewhat high, but wrinkles clearly remained after sitting. The sample was thus unsuitable as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 3. [0129]

COMPARATIVE EXAMPLE 2C

A plain woven fabric was produced using 830 dtex polyester at a density of 28 yarns per inch as both the warp and the weft, and testing was carried out as in Example 1C. The feeling when seated was extremely poor, possibly because the sinking amount was extremely low, and moreover there were wrinkles in the fabric after sitting; the fabric was thus unsuitable as a seat cushioning material for office chairs, household chairs, seats for automobiles or trains, and so on. The details of the yarns, the physical properties of the woven fabric, and the performance are shown in Table 3. [0130]
The following were found from the results for the examples and the comparative examples. The woven fabric in each of Examples 1C to 3C was a woven fabric that uses an elastic yarn comprising two polyether-ester-based elastomers having different melting points to one another as the weft and a polyester yarn as the warp, and for which yarn fixing was carried out by carrying out dry heat treatment, and was designed such that ST1/ST2 is not more than 5. These fabrics used in the examples had a suitable hardness and sinking amount, and the elongation recoverability was satisfactory. Moreover, there was sliding resistance, there was no fraying or yarn slippage, and the feeling when seated was excellent, and hence these woven fabrics satisfied all of the properties required of a cushioning material. [0131]
As with the examples, the woven fabric of Comparative Example 1C was a woven fabric that uses an elastic yarn comprising two polyether-ester-based elastomers having different melting points to one another as the weft and a polyester yarn as the warp, and for which yarn fixing was carried out by carrying out dry heat treatment, but was designed such that ST1/ST2 was greater than 5. The sinking amount for this fabric was somewhat high, and the feeling was not necessarily good. Moreover, wrinkles arose while sitting, and hence it was found that the fabric was unsuitable as a cushioning material. [0132]

With Comparative Example 2C, a polyester yarn was used as both the warp and the weft, and hence the stress at 10% elongation exceeded 600N per 5 cm width in both the warp direction and the weft direction. The sinking amount for this fabric was extremely low, and hence the feeling was extremely poor. Moreover, wrinkles arose while sitting, and hence it was found that the fabric is unsuitable as a cushioning material.

TABLE 3


Example	Example	Example	Comparative	Comparative
1C	2C	3C	Example 1C	Example 2C

Warp
Type	Polyester	Polyester	Polyester	Polyester	Polyester
	yarn	yarn	yarn	yarn	yarn
Fineness	830	830	830	830	830
(dtex)
Number of	70	70	70	70	70
filaments
Strength	8.8	8.8	8.8	8.8	8.8
(cN/dtex)
Elongation	20	250	20	20	20
(%)
Weft
Type	Polyether-	Polyether-	Polyether-	Polyester	Polyether-
	ester-based	ester-based	ester-based	ester-based	yarn
	elastic yarn	elastic yarn	elastic yarn	elastic yarn
Composite	Core-sheath	Core-sheath	Core-sheath	Core-sheath	None
structure	(80:20)	(80:20)	(80:20)	(80:20)
Fineness	2080	2080	2080	2080	830
(dtex)
Number of	1	1	1	1	70
filaments
Strength	2.1	2.1	2.1	2.1	8.8
(cN/dtex)
Elongation	120	120	120	120	20
(%)
Woven fabric
Weave	Plain	2/1 twill	2/1 twill	Plain	Plain
Warp
direction
Density (yarns	28	28	36	32	28
per inch)
Tensile strength	1180	1200	1510	1350	1180
(N/5 cm)
Tensile elongation	40	43	42	40	40
(%)
Stress at 10%	760	760	970	870	760
elongation (N
per 5 cm
width)
Elongation recovery	65	63	64	64	65
factor (%)
Weft direction
Density (yarns	20	20	15	10	28
per inch)
Tensile strength	1200	1200	1200	1200	1180
(N/5 cm)
Tensile elongation	135	138	139	135	40
(%)
Stress at 10%	300	300	220	150	760
elongation (N per
5 cm width)
Elongation recovery	85	84	85	84	65
factor (%)
ST1/ST2	2.5	2.5	4.4	5.8	1.0
Sliding resistance (N)	41	26	21	36	0.6
Sitting
Sinking amount	30	31	34	40	21
(mm)
Feeling	A	A	A	B	D
Recovery from	A	A	A	D	D
wrinkles

According to the present invention, an elastic woven or knitted fabric can be obtained that exhibits excellent elasticity and elastic recoverability with no yarn slippage, and is ideal as a cushioning material. [0134]
Moreover, according to the present invention, an elastic woven or knitted fabric can be obtained that exhibits excellent elasticity and elastic recoverability with no yarn slippage, gives no feeling of stickiness even upon sitting for a prolonged time, and is ideal as a cushioning material. [0135]

Claims

What is claimed is:

2. The elastic woven or knitted fabric according to claim 1, wherein the organic synthetic macromolecule is a polyester-based resin.

3. The elastic woven or knitted fabric according to claim 1, wherein the breaking strength is at least 250N per 5 cm width in each of the warp direction and the weft direction.

4. The elastic woven or knitted fabric according to claim 1, wherein the sliding resistance of the elastic yarn comprising the organic synthetic macromolecule is at least 2N.

5. The elastic woven or knitted fabric according to claim 1, wherein the elastic yarn comprising the organic synthetic macromolecule is a monofilament.

6. A seat cushioning material that uses the elastic woven or knitted fabric according to claim 1.

7. A seat that uses the cushioning material according to claim 6.

8. An elastic woven or knitted fabric that has an elastic yarn comprising an organic synthetic macromolecule disposed in at least part thereof, and has the following physical properties:

(2) an air permeability upon passing through air at a pressure of 125 Pa in a range of 100 to 700 cc/cm²·sec; and

9. The elastic woven or knitted fabric according to claim 8, wherein the organic synthetic macromolecule is a polyester-based resin.

10. The elastic woven or knitted fabric according to claim 8, wherein the breaking strength is at least 250N per 5 cm width in each of the warp direction and the weft direction.

11. The elastic woven or knitted fabric according to claim 8, wherein the sliding resistance of the elastic yarn comprising the organic synthetic macromolecule is at least 2N.

12. The elastic woven or knitted fabric according to claim 8, wherein the elastic yarn comprising the organic synthetic macromolecule is a monofilament.

13. A seat cushioning material that uses the elastic woven or knitted fabric according to claim 8.

14. A seat that uses the cushioning material according to claim 13.

15. A method of manufacturing an elastic woven or knitted fabric, comprising the steps of:

16. The method of manufacturing an elastic woven or knitted fabric according to claim 15, wherein a low-melting-point polyether-ester-based elastomer resin fuses and hardens through the heat treatment at parts of the woven or knitted fabric where the yarns intersect.

17. The method of manufacturing an elastic woven or knitted fabric according to claim 15, wherein the content in the woven or knitted fabric of the elastic yarn comprising the polyether-ester-based elastomers is at least 25 wt %.

18. The method of manufacturing an elastic woven or knitted fabric according to claim 15, wherein the elastic yarn comprising the polyether-ester-based elastomers has a core-sheath structure, and the melting point of a core component polyether-ester-based elastomer is at least 30° C. higher than the melting point of a sheath component polyether-ester-based elastomer.

19. The method of manufacturing an elastic woven or knitted fabric according to claim 18, wherein the weight ratio of the core component to the sheath component is in a range of 95:5 to 30:70.