US20050130539A1 - Nonwoven webs manufactured from additive-loaded multicomponent filaments - Google Patents
Nonwoven webs manufactured from additive-loaded multicomponent filaments Download PDFInfo
- Publication number
- US20050130539A1 US20050130539A1 US10/736,261 US73626103A US2005130539A1 US 20050130539 A1 US20050130539 A1 US 20050130539A1 US 73626103 A US73626103 A US 73626103A US 2005130539 A1 US2005130539 A1 US 2005130539A1
- Authority
- US
- United States
- Prior art keywords
- additive
- surfactant
- concentration
- sheath
- nonwoven web
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Multicomponent filaments for manufacturing a hydrophilic nonwoven web in which each filament has a sheath and a core enclosed within the sheath that includes a concentration of an additive, such as a surfactant. Additive removed from an external surface of the sheath is replaced by additive migrating outwardly from the sheath. Additive migrating outwardly from the core into the sheath, which initially either includes a smaller additive concentration than the core or lacks additive, serves to replenish additive transferred from the sheath to the external surface.
Description
- The invention relates generally to nonwoven webs and, more particularly, to nonwoven webs of multicomponent filaments loaded with surfactant and methods of manufacturing such nonwoven webs.
- Nonwoven webs and their manufacture in meltspinning devices have been the subject of extensive development resulting in a wide variety of materials for numerous commercial applications. Nonwoven webs consist of a sheet of overlapped or entangled filaments or fibers of melt-processable thermoplastic polymers manufactured using spunbond and meltblown processes. A spunbond process generally involves extruding a curtain of semi-solid filaments of one or more thermoplastic polymers from multiple rows of fine orifices in a spinneret and attenuating or drawing the extruded filaments with drag forces created by a high-velocity flow of process air. Spunbond filaments are generally continuous and may have average diameters in the range of about 10 to 20 microns. A meltblown process generally involves pumping a thermoplastic polymer from an extruder through a die to form a curtain of fibers and directing a high pressure gas stream at the exit of a die to attenuate the fibers while they are in their extensible molten state. Meltblown fibers may be continuous or discontinuous and are usually smaller than 10 microns in average diameter. The filaments or fibers are deposited on a moving collector in a substantially random manner thereby forming a continuous-length nonwoven web.
- As many thermoplastic polymers are normally hydrophobic, the thermoplastic filaments or fibers must be modified to produce a nonwoven web that is water permeable or hydrophilic. One modification technique involves mixing a surfactant with the thermoplastic polymer before extrusion so that the fibers or filaments are impregnated with surfactant upon extrusion. The surfactant migrates or diffuses to the external surface of the impregnated fibers or filaments in a process called blooming. Surfactant migration may occur during and/or after filament formation and may be coerced by heating. Alternatively, the filaments or fibers may be surface-treated with a chemical agent by a conventional post-deposition topical treatment. One type of post-deposition surface treatment involves dipping the nonwoven web in a treatment bath containing a surfactant. Another type of post-deposition surface treatment involves coating or spraying the nonwoven web with a treatment solution containing a surfactant.
- Surfactant-treated nonwoven webs in an article are susceptible to surfactant loss when exposed to stresses capable of removing the surfactant. Surfactant may be transferred from the external surface of a surfactant-treated nonwoven web to a contacting hydrophobic material, such as when an article containing the surfactant-treated nonwoven web is packaged and stored. As a specific example, surfactant is transferred from top sheets in hygienic articles to contacting hydrophobic surfaces of the hygienic article and/or to the product packaging when compression packaged and stored before use. As a result, the hygienic article will not perform as expected when used or has a shortened shelf life the top sheet gradually loses its ability to transfer liquids, and. Elevated temperatures experienced during shipping and storage may accelerate surfactant migration to contacting hydrophobic surfaces rendering them hydrophilic with a concomitant loss of barrier properties. The incremental conversion of hydrophobic surfaces further reduces product shelf life.
- Surfactant also tends to be removed from the surfactant-treated nonwoven web by recurring exposure to an aqueous medium. For example, washing cycles gradually diminish the hydrophilicity of a surfactant-treated nonwoven web. As another example, when used as a top sheet in a hygienic absorbent article, a surfactant-treated nonwoven web loses its aqueous permeability with accumulating exposures to soilings by aqueous body fluids.
- It would be desirable, therefore, to provide a nonwoven web treated with a chemical agent or additive, such as a surfactant, that can better withstand stresses and adverse conditions such as those discussed above.
- The invention provides a multicomponent filament having a sheath region of a first melt-processable polymer and a core region of a second melt-processable polymer encased within the sheath region. The core region includes an additive distributed with a first concentration that, over time and with the occurrence of stresses, migrates outwardly from the core region to the sheath region due to the presence of a concentration gradient decreasing in a radially outward direction. The first melt-processible polymer of the sheath region operates to impede the radial migration of additive from the core region to the filament's external surface.
- In certain embodiments of the invention, the sheath region may initially contain a concentration of the additive that is smaller than the first concentration of the additive in the core region. Alternatively, the additive may be absent from the sheath region when the filaments are formed. In other embodiments of the invention, the sheath region may contain a second concentration of an additive that differs in chemical composition from the additive in the core region, where the additives produce the same web characteristic. The additive(s) may be a concentration gradient of surfactant that produces a hydrophilic web or other non-surfactant additives, such as colorants, anti-static agents, lubricants, flame retardants, antibacterial agents, softeners, ultraviolet absorbers, and polymer stabilizers in which the non-surfactant additive migrates from the core region to the sheath region and external filament surface.
- In accordance with the principles of the invention, a nonwoven web is manufactured by heating two thermoplastic polymers to a flowable state and adding a concentration of an additive, such as a surfactant, to at least one of the two thermoplastic polymers. The thermoplastic polymers are combined to form multicomponent filaments each having a core region of the additive-containing thermoplastic polymer and a sheath region of the other thermoplastic polymer, which may also include a concentration of an additive. The multicomponent filaments are collected to form the nonwoven web. If the additive is a surfactant, the period over which the non-woven web exhibits effective hydrophilicity may be extended as the sheath region impedes the radial migration of additive from the core region to the filament's external surface.
- The nonwoven web of the invention may be used in diverse commercial product applications including, but not limited to, hygienic articles such as diapers, adult incontinence products, and feminine hygiene products. Nonwoven webs loaded with surfactant in accordance with the principles of the invention may be used as a top sheet for an absorbent medium in a hygienic article. Articles formed from nonwoven webs of such surfactant-loaded filaments will demonstrate a lengthened shelf life and an improved performance when subject to successive wettings by liquids. Additionally, high fiber basis weight nonwoven webs require an internal surfactant or bloom additive to insure hydrophilicity without the need to fully wet the material with a conventional topical treatment. Such topical treatments are disadvantageous as these relatively-thick nonwoven webs must be dried throughout their full thickness, which is time consuming and adds needless cost to the production of a hydrophilic nonwoven web. In accordance with the invention, the surfactant is not applied topically as a surface treatment and, as a result, the nonwoven web does not have to be dried.
- These and other objects and advantages of the present invention shall become more apparent from the accompanying drawings and description thereof.
- The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and, together with a general description of the invention given above, and the detailed description given below, serve to explain the principles of the invention.
-
FIG. 1 is a diagrammatic view of an apparatus for forming a nonwoven web in accordance with the principles of the invention; -
FIG. 2 is a multicomponent filament in accordance with the principles of the invention; -
FIG. 3 is an axial cross-sectional view of the multicomponent filament ofFIG. 2 ; -
FIGS. 4-6 are end views of multicomponent filaments in accordance with alternative embodiments of the invention; and -
FIG. 7 is a perspective view of a hygienic article in accordance with the principles of the invention. - The invention is directed to nonwoven webs having a lengthened property, such as hydrophilicity, formed from multicomponent filaments including a sheath and a core embedded in the sheath, in which the core has a concentration of an additive, such as surfactant, that serves as a reservoir for replenishing additive depleted from the sheath. Although the invention will be described herein as being manufactured by an exemplary meltspinning system, it should be understood that modifications to the exemplary system described herein could be made so as to conform any portion or the entire system to produce any type of airlaid nonwoven web or a collection of unbonded filaments or fibers without departing from the intended spirit and scope of the invention.
- With reference to
FIG. 1 , aspunbonding apparatus 10 is equipped with a pair of extruders 12, 14 that each convert a solid thermoplastic polymer into a molten state and provide the molten thermoplastic polymers under pressure to a corresponding set ofgear pumps 16,18. Extruder 12 is provided initially with a solid mass of Polymer A from abulk source 20, and extruder 14 is provided initially with a solid mass of Polymer B from abulk source 22, which are replenished frombulk sources gear pumps 16, 18 pump metered amounts of each thermoplastic polymer to an extrusion die or spinneret 24, which has a spin pack that combines the thermoplastic polymers and discharges a curtain ofmulticomponent filaments 26 constituted collectively by the two thermoplastic polymers. For ease of reference, one thermoplastic polymer provided to spinneret 24 will be referred to as Polymer A, while the second thermoplastic polymer provided to spinneret 24 will be referred to as Polymer B. As will be understood in accordance with the principles of the invention, other embodiments may utilize more than two thermoplastic polymers. An exemplary multiple-component spin pack for aspinneret 24 is disclosed in U.S. Pat. No. 5,162,074, which is hereby incorporated by reference herein in its entirety. - The descending airborne curtain of
multicomponent filaments 26 are quenched with cross-flow cooling air, as represented byarrows 28, from a quench blower (not shown) to accelerate solidification and drawn through a filament-drawing device 30. The filament-drawing device 30 applies a tangential high velocity flow of process air, as represented byarrows 31, in a direction substantially parallel to the length of themulticomponent filaments 26. Because themulticomponent filaments 26 are extensible, the drag force of the spunbonding process pneumatically attenuates and molecularly orients themulticomponent filaments 26. Themulticomponent filaments 26 discharged from the filament-drawingdevice 30 are deposited in a substantially random manner as anonwoven web 32 on a horizontally and linearly moving perforatedcollector 34. Thecollector 34 moves in a machine direction, represented by the arrow labeled MD, that represents the length of thenonwoven web 32 in the direction in which it is produced. Thecollector 34 also spans the width of the curtain ofmulticomponent filaments 26 in a cross-machine direction perpendicular to the machine direction and into and out of the plane of the page ofFIG. 1 . - Additional spunbonding apparatus, not shown but similar to
spunbonding apparatus 10, and meltblowing apparatus (not shown) may be provided downstream ofspunbonding apparatus 10 for depositing one or more spunbond and/or meltblown nonwoven webs of either monocomponent or multicomponent filaments onnonwoven web 32. An example of such a multilayer laminate in which some of the individual layers are spunbond and some meltblown is a spunbond/meltblown/spunbond (SMS) laminate made by sequentially depositing onto a moving forming belt first a spunbond fabric layer, then a meltblown fabric layer and last another spunbond layer. - With continued reference to
FIG. 1 , a surfactant from asurfactant source 36 is added along with the mass of Polymer B frombulk source 22 to the hopper of extruder 14. A mass or volume of the surfactant is blended, preferably homogenously, with Polymer B to create a mixture that is pumped by gear pump 18 from the extruder 14 to thespinneret 24. The surfactant may be any suitable chemical agent that increases the hydrophilicity of themulticomponent filaments 26 so thatnonwoven web 32 is wettable by and has the strong ability to absorb an aqueous medium containing water or another liquid. A mass or volume of a surfactant from adifferent surfactant source 38 may be mixed with the mass of Polymer A frombulk source 20 added to the hopper of extruder 12 and pumped by gear pump 18 from extruder 12 tospinneret 24. In this manner and consistent with the principles of the invention, each of the thermoplastic polymers provided to thespinneret 24 may include a surfactant concentration. - The surfactant may be blended with the thermoplastic polymer in a dry form, such as powder or pellets, using conventional mechanical mixing techniques before being placed into the hopper of either extruder 12, 14. Mechanical mixing techniques using devices for homogenizing an admixture of powders and pellets, such as V-blenders or double cone blenders, are familiar to persons of ordinary skill.
- The melt-processable thermoplastic polymer or polymers used to fabricate the
multicomponent filaments 26 may be any of the commercially available spunbond grades of a wide range of thermoplastic polymer resins, copolymers, and blends of thermoplastic polymer resins, including without limitation polyolefins such as polyethylene and polypropylene, polyesters such as polyethylene terephthalate, polybutylene, polyamides, nylons, polyvinyl acetate, polyvinyl chloride, polyvinyl alcohol, cellulose acetate, and blends and copolymers thereof. The invention contemplates that each of the thermoplastic polymers (Polymers A and B) constituting themulticomponent filaments 26 may be identical in base composition and differ only in the concentration of the added surfactant. For example, the core may be formed from polypropylene containing a concentration of surfactant and the sheath may be formed from polypropylene having identical material characteristics and a lower concentration of surfactant. Most of these thermoplastic polymer resins are hydrophobic and, therefore, are rendered hydrophilic (wettable) by the presence of the surfactant at the external surface. The surfactant may also be added to normally hydrophilic thermoplastic resins for enhancing their wettability. - Typically, the surfactants supplied by the
surfactant sources nonwoven web 32 at a fast rate or, alternatively, as a low wetting surfactant which causes liquids to permeate thenonwoven web 32 at a relatively slow rate. Each surfactant must be miscible with the associated thermoplastic polymer so as to be capable of forming homogeneous mixtures. Each surfactant may be anionic, cationic, amphoteric or non-ionic, in which non-ionic surfactants are believed to be less irritating to human skin tissue. Preferred non-ionic surfactants include, but are not limited to, sorbitan esters, ethoxylated sorbitan esters, silicone copolymers, fluorochemical-based surfactants, alcohol ethoxylates, alkylphenol ethoxylates, carboxylic acid esters, glycerol esters, polyoxyethylene esters of fatty acids, polyoxyethylene esters of aliphatic carboxylic acids related to abietic acid, anhydrosorbitol esters, ethoxylated anhydrosorbitol esters, ethoxylated natural fats, oils, and waxes, glycol esters of fatty acids, carboxylic amides, diethanolamine condensates, monoalkanolamine condensates, polyoxyethylene fatty acid amides, and polyalkyleneoxide block copolymers. - With reference to
FIGS. 2 and 3 , the thermoplastic polymers constituting eachmulticomponent filament 26 are arranged a sheath/core configuration in which one thermoplastic polymer (Polymer B) is disposed in a core 40 surrounded by asheath 42 of the other thermoplastic polymer (Polymer A). Thecore 40 andsheath 42 each extend continuously along the length of eachmulticomponent filament 26 and are coextensive along an annular orcylindrical interface 43. Thecore 40 andsheath 42 may be arranged coaxially in a concentric configuration with thesheath 42 radially outward of thecore 40. - In accordance with the principles of the invention and with reference to
FIGS. 2 and 3 , asurfactant 44 a is present in the core 40 in a greater concentration than asurfactant 44 b insheath 42. Preferably, the concentration ofsurfactant 44 a in Polymer B constituting thecore 40 is about 5% by weight to about 10% by weight, and the concentration ofsurfactant 44 b in Polymer A constituting thesheath 42 ranges up to about 3% by weight, typically about 1% by weight to about 3% by weight. In certain specific embodiments of the invention, Polymer A may be the same thermoplastic polymer as Polymer B and the chemical composition of the surfactant in each of the polymers may be identical. - In accordance with the principles of the invention, the
surfactant 44 a initially present in the core 40 will tend to diffuse or migrate from the region of high concentration across theinterface 43 to the region of low concentration in thesheath 42, as represented by the arrows labeled with reference numeral 41. Molecules ofsurfactant 44 b initially present at anexternal surface 48 of thesheath 42 produce hydrophilicity or wettability. Surfactant molecules at theexternal surface 48 of thesheath 42 are lost, as represented by the arrows labeled withreference numeral 47, by contact with another hydrophobic surface or by repeated wetting with liquid. Amounts ofsurfactant 44 b andsurfactant 44 a present insheath 42 migrate to theexternal surface 48 as represented by the arrows labeled withreference numeral 49. The radially outward migration reduces the surfactant concentration in thesheath 42. As the surfactant concentration drops in thesheath 42,surfactant 44 a migrating from the core 40 into thesheath 42 replenishes the depleted concentration ofsurfactant 44 a andsurfactant 44 b. As a result, the nonwoven web 32 (FIG. 1 ) will remain hydrophilic for a, longer period after manufacture when packaged and with repeated exposure to liquids. Thesurfactant 44 a in thecore 40 serves as a reservoir for surfactant transfer, as required or otherwise on a time-delayed basis due to the difference in concentration, across theannular interface 43 to thesheath 42 and subsequently to theexternal surface 48. - With reference to
FIG. 4 and in accordance with an alternative embodiment of the invention,sheath 42 may contain nosurfactant 44 b at least at the moment of discharge from the spinneret 24 (FIG. 1 ).Surfactant 44 a migrates from the core 40 into thesheath 42 and subsequently to theexternal surface 48 makes themulticomponent filament 26 hydrophilic. The initial migration occurs subsequent to discharge of themulticomponent filament 26 from thespinneret 24, such as during web processing to complete web formation, during web processing to form an article, and while the web and/or article are stored before the time of use. - The invention contemplates that the chemical composition of the
surfactant 44 a may differ from the chemical composition of thesurfactant 44 b. In this alternative embodiment,surfactant 44 a is not present in the sheath 42 (i.e., has a zero concentration) at least at the moment of discharge from the spinneret 24 (FIG. 1 ). The hydrophilicity of themulticomponent filament 26 is supplied initially by molecules ofsurfactant 44 b present at theexternal surface 48. Due to the concentration disparity,surfactant 44 a migrates radially outwardly from the core 40 into thesheath 42 and amounts ofsurfactant 44 a eventually reach theexternal surface 48. Eventually,surfactant 44 a is lost from theexternal surface 48 along with withsurfactant 44 b. Amounts ofsurfactant 44 b lost from theexternal surface 48 are replenished by the outward migration of stored amounts ofsurfactant 44 b from thesheath 42.Surfactant 44 a lost from theexternal surface 48 is replenished by amounts ofsurfactant 44 a migrating from the underlyingsheath 42. The store ofsurfactant 44 a in thesheath 42 is replenished by migration of amounts ofsurfactant 44 a fromcore 40. The migration and loss ofsurfactant 44 a may be independent of the migration and loss ofsurfactant 44 b or the migration and loss ofsurfactants 44 a,b may be interrelated. - By adjusting the relative concentrations of the
surfactants 44 a,b in the two thermoplastic polymers (Polymers A and B), the shelf life of the surfactant-treatednonwoven web 32 may be significantly extended as the hydrophilic nature of theexternal surface 48 is lengthened by the net transport or migration ofsurfactant 44 a from the relatively-high surfactant concentration present in the core 40 into thesheath 42 and to theexternal surface 48. In addition to the gradient in surfactant concentration, the migration rate from the core 40 to thesheath 42 and from thesheath 42 to theexternal surface 48 is also influenced by other factors, including the sheath thickness, the chemical properties of the surfactant(s), the environmental temperature, extrusion conditions, and the characteristics of the thermoplastic polymer(s). In particular, the diffusion of a surfactant in a thermoplastic polymer depends upon the affinity between the surfactant and the thermoplastic polymer. The affinity varies among the different possible combinations of thermoplastic polymer and surfactant, which will influence transfer ofsurfactant 44 a from the core 40 to thesheath 42 andsurfactant 44 a andsurfactant 44 b from thesheath 42 to the external surface. Accordingly, the affinity between the selected surfactant and the thermoplastic material forming the core 40 should permit surfactant transfer from the core 40 to thesheath 42. Likewise, the affinity between the thermoplasticpolymer forming sheath 42 andsurfactant 44 a will influence migration ofsurfactant 44 a from thesheath 42 to theexternal surface 48. Similarly, the affinity between the thermoplasticpolymer forming sheath 42 andsurfactant 44 b will influence migration ofsurfactant 44 b from thesheath 42 to theexternal surface 48. - The invention contemplates that one or more non-surfactant additives, such as compatibilizing agents, colorants or pigments, optical brighteners, ultraviolet light stabilizers, antistatic agents, abrasion resistance enhancing agents, nucleating agents, fillers and/or other additives and processing aids, may be added in a concentration gradient to one or more of the polymers constituting
multicomponent filaments 26. In these various alternative embodiments, the non-surfactant additive is added tofilaments 26 with a greater concentration in the core 40 than in thesheath 42, as described herein with specific regard to surfactant. The subsequent additive migration of the non-surfactant additive(s) radially outward from thecore 40 lengthens or sustains the manifestation of a corresponding property(ies) or a characteristic(s) of thefilaments 26. The invention contemplates that one or more of the non-surfactant additives may be distributed inmulticomponent filaments 26 in a manner similar to the concentration gradient of surfactant, as described herein, either jointly with the surfactant or in the absence of surfactant. - With reference to
FIG. 5 and in accordance with an alternative embodiment of the invention,multicomponent filament 26 may have a core 50 that is offset or non-concentric within asheath 52 so as to have an eccentric or asymmetrical configuration. With reference toFIG. 6 and in accordance with another alterative embodiment of the invention, the thermoplastic polymers ofmulticomponent filament 26 may have an “islands-in-the-sea” configuration in whichmultiple core regions 60 of Polymer B reside inside asheath 62 of Polymer A. Although the components offilament 26 are depicted inFIGS. 2-6 as having round cross-sections, the invention contemplates that thenonwoven web 32 might be formed from filaments (not shown) of different cross-sectional shapes. - With reference to
FIG. 7 , a disposablehygienic article 70 generally includes atop sheet 72, aback sheet 74, afluid storage layer 76 separating thetop sheet 72 from theback sheet 74, and a fluid acquisition andtransfer layer 78 separating thefluid storage layer 76 from thetop sheet 72. Thetop sheet 72, which faces and contacts the wearer, is fluid previous so that aqueous body fluids may readily penetrate through its thickness to thefluid storage layer 76. Fluid acquisition andtransfer layer 78 distributes aqueous body fluids transferred fromtop sheet 72 to the underlyingfluid storage layer 76, which includes an absorbent material capable of absorbing large quantities of aqueous body fluids and retaining the absorbed body fluids under moderate applied pressures. Theback sheet 74 prevents aqueous body fluids absorbed in thefluid storage layer 76 from wetting items in the surrounding environment, such as pants, pajamas and undergarments. Loop-type fasteners 80 on theback sheet 74 cooperate with hook-type fasteners 82 on correspondingattachment tabs 84 extending laterally of theback sheet 74 cooperate for attaching thehygienic article 70 to a wearer. - In accordance with the principles of the invention, all or part of the components of
hygienic article 70, including but not limited to thetop sheet 72 and theback sheet 74, may incorporate portions of a nonwoven web formed from the multicomponent filaments of the invention. The invention contemplates that various other consumer and commercial articles may incorporate a portion of a nonwoven web formed from the multicomponent filaments of the invention. - While the present invention has been illustrated by a description of various embodiments and while these embodiments have been described in considerable detail, it is not the intention of the applicants to restrict or in any way limit the scope of the appended claims to such detail. Additional advantages and modifications will readily appear to those skilled in the art. For example, the multicomponent filaments from which the nonwoven web of this invention is made may be produced by meltblown processes as well known to persons of ordinary skill in the art. The invention in its broader aspects is therefore not limited to the specific details, representative apparatus and methods, and illustrative examples shown and described. Accordingly, departures may be made from such details without departing from the spirit or scope of applicants' general inventive concept. The scope of the invention itself should only be defined by the appended claims, wherein we claim:
Claims (13)
1. A nonwoven web comprising a plurality of multicomponent filaments, each of the multicomponent filaments comprising:
a sheath region including a first melt-processable polymer; and
a core region encased within said sheath region, said core region including a second melt-processable polymer and a first additive distributed at a first concentration in said second melt-processable polymer, said first additive migrating outwardly from said core region into said sheath region.
2. The nonwoven web of claim 1 wherein said first melt-processable polymer includes a second concentration of said first additive, said second concentration being less than said first concentration to produce a concentration gradient.
3. The nonwoven web of claim 2 wherein said first concentration of said first additive ranges from about 5% by weight to about 10% by weight and said second concentration of said first additive is less than about 3% by weight.
4. The nonwoven web of claim 1 wherein said first melt-processable polymer includes a second concentration of a second additive differing in chemical composition from said first additive.
5. The nonwoven web of claim 1 wherein said first concentration of said first additive ranges from about 5% by weight to about 10% by weight.
6. The nonwoven web of claim 1 wherein said first additive is a surfactant selected from the group consisting of an anionic surfactant, a cationic surfactant, an amphoteric surfactant, and a non-ionic surfactant.
7. The nonwoven web of claim 1 wherein said sheath region and said core region are concentrically arranged.
8. The nonwoven web of claim 1 wherein said core region has an eccentric arrangement with said sheath region.
9. The multicomponent filament of claim 1 further comprising a plurality of core regions within said sheath region, at least one of said core regions including said first additive.
10. The multicomponent filament of claim 1 wherein said sheath region has an external surface and a portion of at least said first additive is chemically active at said external surface, after outward migration has occurred.
11. A method of manufacturing a nonwoven web, comprising:
heating a first thermoplastic polymer to a flowable state;
heating a second thermoplastic polymer to a flowable state;
adding a first concentration of a first additive to the first thermoplastic polymer;
combining the first and second thermoplastic polymers to form a plurality of multicomponent filaments each having a sheath region including the second thermoplastic polymer and a core region including the first thermoplastic polymer and the first additive; and
collecting the plurality of multicomponent filaments to form a nonwoven web.
12. The method of claim 11 further comprising:
adding a second concentration of the first additive to the sheath region, the second concentration being smaller than the first concentration.
13. The method of claim 11 further comprising:
adding a second concentration of a second additive to the sheath region.