US20120282711A1 - Magnetic tunnel junction (mtj) formation using multiple etching processes - Google Patents
Magnetic tunnel junction (mtj) formation using multiple etching processes Download PDFInfo
- Publication number
- US20120282711A1 US20120282711A1 US13/371,380 US201213371380A US2012282711A1 US 20120282711 A1 US20120282711 A1 US 20120282711A1 US 201213371380 A US201213371380 A US 201213371380A US 2012282711 A1 US2012282711 A1 US 2012282711A1
- Authority
- US
- United States
- Prior art keywords
- layer
- mtj
- manufacturing
- recited
- forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- This application is a continuation-in-part (CIP) of U.S. patent application Ser. No. 13/100,048, filed on May 3, 2011, by Abedifard et al., and entitled “Magnetic Tunnel Junction (MTJ) Formation With Two-Step Process”, incorporated herein by reference as though set forth in full.
- 1. Field of the Invention
- The invention relates generally to non-volatile magnetic memory and particularly to manufacturing magneto (also referred to as “magnetic”) tunnel junction (MTJ) included in the non-volatile magnetic memory.
- 2. Description of Prior Art
- It is well known that current memory is experiencing its manufacturing limitations and is subject to dramatically change in the coming years. Magnetic memory offers an alternative to replacing current memory however, manufacturing of magnetic memory, such as magnetic random access memory (MRAM), is experiencing its own set of problems. Challenges, not easy to overcome, remain largely in the fabrication of scalable and reliable magneto (also referred to as “magnetic”) tunnel junction (MTJ), an active and vital part of the MRAM. An MRAM element is typically made of MTJ and surrounding layers, all formed on a substrate. The MTJ generally serves to save information or data by changing its magnetic orientation, which in some MTJs occurs upon the flow of suitable electrical current through the MTJ.
- In these types of MTJs, the MTJ is typically made of a fixed layer, fixed in its magnetic orientation, a barrier layer, and a free layer whose magnetic orientation defines the state of the MTJ's and is switchable according to the current flowing therethrough, relative to the magnetic orientation of the fixed layer.
- A tantalum layer is typically formed on top of the MTJ and used to establish a connection to the MTJ for incorporating the MTJ in the MRAM . As discussed above, the MTJ is made of a free layer, typically formed below the tantalum layer, a barrier or MgO layer, formed below the free layer, and a fixed layer formed under the MgO layer. The barrier layer is obviously not a metal layer whereas the free and fixed layers are made of metal. Various layers are formed below the fixed layer and above a metal layer, within or above the substrate, in an effort to help the fixed layer maintain its permanent magnetic orientation. During manufacturing, when etching to form the magnetic memory element (or MRAM element), the metals of the layers below the MgO layer, including the metal layer (typically made of copper) result in some of the metal being re-deposited onto the MgO layer therefore undesirably causing shorting. That is, this detrimentally causes defective MRAM elements because the fixed and free layers are effectively shorted together across the barrier (MgO) layer that is positioned between the fixed and free layers.
- What is needed is reliable manufacturing of MRAM elements.
- To overcome the limitations in the prior art described above, and to overcome other limitations that will become apparent upon reading and understanding the present specification, the present invention discloses a method and a corresponding structure for a magnetic storage memory device and a method of manufacturing the same that is reliable.
- Briefly, a method of manufacturing a magnetic memory element includes the following steps. The manufacturing of a magnetic memory element includes the steps of forming a permanent magnetic layer on top a bottom electrode, forming a pinning layer on top the permanent magnetic layer, forming a magnetic tunnel junction (MTJ) including a barrier layer on top of the pinning layer, forming a top electrode on top of the MTJ, forming a hard mask on top of the top electrode, and using the hard mask to perform a series of etching processes to reduce the width of the MTJ and the top electrode to substantially a desired width, where one of these etching processes is stopped when a predetermined material in the pinning layer is detected thereby avoiding deposition of metal onto the barrier layer of the etching process thereby preventing shorting.
- These and other objects and advantages of the present invention will no doubt become apparent to those skilled in the art after having read the following detailed description of the preferred embodiments illustrated in the several figures of the drawing.
-
FIG. 1 shows aMRAM element 10, in accordance with a method and embodiment of the present invention. -
FIG. 2 shows theMRAM element 10 after etching of theoxide layer 22. -
FIG. 3 shows the step of depositing photo-resist 32 on top of and around the portion of theoxide layer 30 after the etching step ofFIGS. 2 and 3 . -
FIG. 4 shows theelement 10 after the etching step ofFIG. 3 . -
FIG. 5 shows theelement 10 after the etching step ofFIG. 4 . -
FIG. 6 shows aMRAM element 50, in accordance with an embodiment and method of the present invention. -
FIGS. 7-11 show an alternative embodiment and method employed to manufacture theMRAM element 50, -
FIGS. 12-18 show the steps employed in manufacture theMRAM element 10, in accordance with a method of the invention. - In the following description of the embodiments, reference is made to the accompanying drawings that form a part hereof, and in which is shown by way of illustration of the specific embodiments in which the invention may be practiced. It is to be understood that other embodiments may be utilized because structural changes may be made without departing from the scope of the present invention.
- A method of manufacturing a magnetic memory element is disclosed. During a first etching step, an oxide layer is etched using a first photo-resist, to leave a portion of the oxide layer, the portion of the oxide layer has a length and a width. The oxide layer is formed on top of a contact layer, the contact layer is formed on top of a free layer, the free layer is formed on top of a barrier layer, the barrier layer is formed on top of a fixed layer, and the fixed layer is formed on top of a metal layer. The metal layer is deposited along the plane of a substrate. The free layer, barrier layer and fixed layer define a magneto tunnel junction (MTJ) and the MTJ and contact layer define a MTJ stack. The width of the portion of the oxide layer is defined along the plane of the substrate and has a size that is substantially the size of a desired width of the free layer after manufacturing of the magnetic memory element. The length of the portion of the oxide layer is substantially perpendicular to the width thereof where the length of the portion of the oxide layer extends from the top of the contact layer to the bottom of the first photo-resist. Additionally, a second photo-resist is deposited on top of and around the portion of the oxide layer and a second etching step is performed of the MTJ stack, using the second photo-resist, to leave a portion of the contact layer, a portion of the free layer and a portion of the barrier layer, each of the portion of the contact layer, free layer and barrier layer having a width equal to the width of the second photo-resist. A third etching is performed of the MTJ stack, using the portion of the oxide layer, to leave a second portion of the contact layer, a second portion of the free layer and a second portion of the barrier layer, each of the second portion of the contact layer, free layer and barrier layer having a width equal to the width of the portion of the oxide layer.
- In some methods of the present invention, during the second etching step, a portion of the fixed layer and layers under the fixed layer are etched.
- In some methods of the present invention, during the third etching step, etching is stopped after etching the barrier layer and the fixed layer and layers under the fixed layer are not etched.
- Accordingly, since during the second etching step, the fixed layer and layers under the fixed layer are not etched, a significantly larger portion (as an example Ta layer) of the contact layer remains after all etching steps are completed that is better suitable for connecting the MTJ to circuits outside of the magnetic memory element.
- Referring now to
FIG. 1 , in accordance with a method and embodiment of the present invention, aMRAM element 10 is shown where theMRAM element 10, at this step and during the formation thereof, is shown to include abottom electrode 14, afixed layer 15, abarrier layer 16, afree layer 17, and acontact layer 18. Thelayers oxide layer 22 is shown formed on top of thecontact layer 18. A photo-resist 24 is shown formed on a portion of theoxide layer 22. Optionally, anitride layer 20 is formed on top of thecontact layer 18 and below theoxide layer 22. Additionally optionally, a tantalum nitride layer (not shown inFIG. 1 ), is formed on top of themetal layer 12 and below thebottom electrode 14. It is understood that themetal layer 12 is formed on top of a substrate not shown inFIG. 1 . - In some embodiments, the
contact layer 17 is made of tantalum (Ta). In some embodiments, thebottom electrode 14 is made of Ta and themetal layer 12 is made of copper. - In those embodiments and methods where a tantalum nitride layer is employed, the tantalum nitride layer serves to protect the
metal layer 12 and prevent it from oxidizing particularly during the times that the wafer is unused and idle during manufacturing, or during transportation as theelement 10 is currently made in different fabrication facilities, in different stages, and is therefore subject to transportation damage. The various methods of the present invention serve to minimize and in some cases eliminate such damage. - The photo-
resist 24 serves as a mask during etching of theoxide layer 22, which is performed to remove theoxide layer 22 except in a portion that is directly below the photo-resist 24 extending therebelow to the top of thenitride layer 20, in embodiments using this layer, otherwise extending to the top of thecontact layer 18. In the dimension that is along the plane of the substrate, the portion of theoxide layer 22 that remains after etching is substantially the size of the width of the photo-resist 24 (along the x-axis inFIG. 1 ). The portion of theoxide layer 22, shown byreference number 30, inFIG. 2 , remains after this etching process - In some embodiments and methods, the
oxide layer 22 is etched with compounds containing fluoride (F), such as Carbon tetra fluoride (CF4) or Sulfa hexa fluoride (SF6), or Tri-Chloro-Fluoro-methane (also referred to as “Freon (CC13F)”). In some methods and embodiments, Ethel alcohol (C2H5OH) or CO with NH3 (Carbon mono-oxide with Amonia) is used to etch the free layer, the fixed layer and the barrier layer. -
FIG. 2 shows theMRAM element 10 after etching of theoxide layer 22, using the photo-resist 24. As shown, the portion of theoxide layer 30 remains and is used for further etching as will be evident shortly. During the foregoing etching step, the photo-resist 24 is essentially also etched in its entirety. -
FIG. 3 shows the step of depositing photo-resist 32 on top of and around the portion of theoxide layer 30 after the etching step ofFIGS. 2 and 3 . This is accomplished by deposition of photo resist and its exposure to the proper mask, in which all the ultraviolet (UV) light-exposed photo resist is developed away other than theportion 32 that is left unexposed to UV light. As shown, because the photo-resist 32 is formed around theoxide layer 30, some of it also covers a portion of the top of thelayer 20. The photo-resist 32 serves as a mask to prevent removal of the portion of the layers thereunder up to thelayer 12, during the next etching step. After the deposition of the photo-resist 32, the MTJ stack, defined by thebottom electrode 14, the MTJ and thecontact layer 18 and in those cases where thenitride layer 20 is used, thenitride layer 20, is etched using carbon tetra fluoride (CF4) to form the structure shown inFIG. 4 . -
FIG. 4 shows theelement 10 after the etching step ofFIG. 3 . Theelement 10 is shown to include thelayer 12 and the portion of theoxide layer 30 and the photo-resist 32, but only a remaining portion of thelayers FIG. 3 defined by the dimension of the photo-resist 32. That is, they each have the same width as the width of the photo-resist 32, assuming width is along the x-axis, and a length, along with y-axis, defined from the bottom of the photo-resist 32 and extending to the top of thelayer 12. - Optionally,
layer 14 is used to stop the foregoing etching thereby leaving thelayer 14 unetched and serving as a stop layer. Still optionally, thelayer 14 is comprised of multiple layers with each layer being made of a different material and the bottom layer of thelayer 14 serving as the stop layer with all other layers etched. - Next, another etching process is performed, using the photo-resist 32 as a mask to prevent removal of a certain desired portion of the
layers free layer 17, which due to its switchable characteristic needs to have a certain area to allow sufficient current drivability but as small as possible to maintain switching current levels low. During the foregoing etching process, the fixedlayer 15 need not be etched because it does not switch in its magnetic orientation once theelement 10 is manufactured. However, the photo-resist 32 itself and the portion of theoxide layer 30 are removed during this etching step. The resulting structure of theelement 10, after the foregoing etching step, is shown inFIG. 5 . -
FIG. 5 shows theelement 10 after the etching step ofFIG. 4 . As stated above, thelayers nitride layer 20′, thecontact layer 18′, thefree layer 17′ and thebarrier layer 15′, each having a width defined by the width of the portion of theoxide layer 30 and a length that is substantially the same as the length they started with upon formation thereof. This advantageously substantially holds the length of thecontact layer 17 in place with small reduction thereof thereby avoiding shorting of the fixedlayer 14 when the MTJ of theelement 10 is connected with circuitry outside of theelement 10. In some embodiments, where the length of thecontact layer 17 is approximately 600 Angstroms, the length of thecontact layer 17′, after the foregoing etching processes, is in the range of 400 to 500 Angstroms whereas prior art techniques reduce the length of this layer to a range of 100 to 200 Angstroms due to etching. This near four time increase in the length of the contact layer allows for reliable connection of the layer 18 (Ta layer) to the other elements of the MRAM. - In embodiments using the
layer 14 as a stop layer, as discussed above, thelayer 14 is etched with some portions removed and some remaining, as shown inFIG. 5 . - It is noted that the
layer layers 17′, 18′ and 20′. -
FIG. 6 shows aMRAM element 50, in accordance with an embodiment and method of the present invention. TheMRAM element 50, at this juncture, during the formation thereof, is shown to include a fixedlayer 56 on top of which is shown formed abarrier layer 57, on top of which is shown formed afree layer 57, forming the MTJ of theelement 50. Further shown issubstrate 66 into a part of which ametal layer 64 is formed. On top of thelayer 64 and thesubstrate 66 is shown formed abottom electrode 52, on top of which is shown formed a contact layer, on top of which is shown formed thelayer 56. Further shown is thetantalum layer 60 on top of thelayer 58, and anoxide layer 62 formed on top of thelayer 60. Theoxide layer 62 serves as a hard mask protecting the Ta layer. - In some embodiments, the
substrate 66 is made of oxide and the contact layer is made of Ta and thelayer 64 is made of copper. - In some embodiments, the thickness of the
layer 60 is greater than the thickness of thelayer 54. -
FIGS. 7-11 show the steps employed to manufacture theMRAM element 50, in accordance with a method of the present invention. - During the
step 70, shown inFIG. 7 ,photoresist 68 is deposited on a portion of the top of thelayer 62 and serves as the MTJ mask to protect a portion oflayer 62 from being etched. During this step, thephotoresist 68 is developed, as a mask, by being exposed. Next, atstep 80, an etching process is performed to etch thelayer 62 in areas not covered by thephotoresist 68. The etching process, in some method, is reactive ion etching (RIE). Further, thephotoresist 68 is also cleaned and removed because it is no longer needed to protect the layers thereunder. Further, another etching process is performed to etch thelayer 60. The Ta layer is etched with RIE using CF4 or CC14 or similar gases. - Next, at
step 80 ofFIG. 8 , theMTJ 51 is etched using C2H5OH or CO and NH3. In the foregoing etching steps, theMTJ 51,layer 60 andlayer 62 are etched to remove them but not in their entirety, rather, the portion of these layers that are below thephotoresist 68 and have a width substantially equal to the width of thephotoresist 68 remains after etching. The portions of these layers that remain are referred to herein as theMTJ 51′, thetantalum layer 60′ and theoxide layer 62′. - Next, at
step 90 ofFIG. 9 ,photoresist 92 is deposited on a portion of the top of thelayer 62′. The width of thephotoresist 92 defines the desired width of the MTJ after completion of manufacturing thereof. Thephotoresist 92 serves as a mask, as thephotoresist 68 did. Thus, this process uses double-mask for defining the ultimate MTJ. Thephotoresist 92, similar to thephotoresist 68 is developed by masking theMTJ 51 and exposing. -
FIG. 10 shows thenext step 100 that is performed where thelayer 62′ is etched to remove this layer but only in areas that are not under thephororesist 92. The area of thelayer 62′ that removes is referred to asoxide layer 62″. The same etching method as that used to etch thelayer 68 is used. Further, thephotoresist 92 is removed/cleaned. -
FIG. 11 shows thenext step 110, where thelayer 60′ is etched and theMTJ 51′ is etched using the same etching methods as that of theelement 10. These layers are etched to leave behindMTJ 51″ having a width substantially the same as the width of thephotoresist 62″. The remaining portions of these layers is referred to as fixedlayer 56′,barrier layer 57′ andfree layer 58, which collectively form theMTJ 51″. Further,tantalum layer 60″ remains. - Further after this step, the
layer 52 and the contact layer are not etched and are left intact, referred to ascontact layer 54′ andlayer 52′. - It is noted that optionally, not all of the MTJ is etched, rather; at least the free layer of the MTJ is etched. It is also noted that during this step, etching causes removal of the
layer 62′ in substantially its entirety. The etching used during this step is similar to that which is described relative toFIGS. 4 and 5 . - In another method of manufacturing a magnetic memory element, in accordance with another method of the invention, a bottom electrode is formed on top a metal layer, followed by forming a permanent magnetic layer on top the bottom electrode, and forming a pinning layer on top the permanent magnetic layer, forming a magnetic tunnel junction (MTJ) including a barrier layer on top of the pinning layer, forming a top electrode on top of the MTJ, forming a hard mask on top of the top electrode, and using the hard mask to perform a series of etching processes to reduce the width of the MTJ and the top electrode to substantially a desired width, where one of these etching processes is stopped when a predetermined material in the pinning layer is detected thereby avoiding deposition of metal onto the barrier layer of the etching process thereby preventing shorting.
-
FIGS. 12-18 show the steps employed in manufacture theMRAM element 110, in accordance with a method of the invention. - Referring now to
FIG. 12 , in accordance with a method and embodiment of the invention, aMRAM element 110 is shown where theMRAM element 110, at this step and during the formation thereof, is shown to include acontact layer 124, shown partially formed on top of a metal layer (M1) 126. Further, theelement 110 is shown to have a permanentmagnetic layer 122 formed on top of theseed layer 124, a pinninglayer 120 formed on top of thelayer 122, a fixedlayer 118 formed on top of thelayer 120, abarrier layer 16 formed on top of thelayer 118, afree layer 114 formed on top of thelayer 116, and atop electrode 112 formed on top of thelayer 114. Thelayer 124 is also referred to herein as the “bottom electrode” or “BE” or “seed” layer. It is noted that in some embodiments, thebottom electrode 124 also serves as a seed layer for proper crystallization of the layers that are formed on top of it. Thelayers element 110. - The
layer 120 magnetically couples the permanentmagnetic layer 122 to the fixedlayer 118 thereby preventing the fixedlayer 118 from changing its magnetic orientation. - A photo-resist 30 is shown formed on a portion of the
oxide layer 128. Optionally, a nitride layer may be formed on top of thelayer 124 and below thelayer 122. Additionally optionally, a tantalum nitride layer (not shown inFIG. 12 ), is formed on top of themetal layer 126 and below thebottom electrode 24. It is understood that themetal layer 112 is formed on top to make connection to MTJ. - In some embodiments, the
layer 124 and the top electrode are each made of tantalum (Ta) and themetal layer 126 is made of copper. Further, in some embodiments, thelayer 122 is made of the alloy cobalt-iron-boron (Co—Fe—B) and similarly, thelayers layer 120 , the pinning layer is made of platinum-manganese (Pt—Mn). - The layers shown in
FIG. 12 are of suitable thickness and sizes. - The
layer 126 is a metal inter-connect layer and is typically formed in or on the substrate (not shown) and is commonly referred to as “Mx” or metal layer, serving to connect theelement 10 with other circuitry (not shown) such as control circuits, access transistor, and the like. Theelement 110, inFIG. 12 , is etched with the result of this etching process shown inFIG. 13 . -
FIG. 13 shows deposition of thehard mask 128 and the photo-resist 130 on top the structure ofFIG. 1 . The hard mask material could be oxide or nitride or variety of other materials, in some cases it can be illuminated totally, and use the photo-resist only. Further shown inFIG. 13 , are the results of the etching of the hard mask, referred to above with reference toFIG. 12 , Theline 140 is shown to merely indicate the level at which the MTJ layers are deposited and is not intended as a part of the structure of theelement 110. Upon the completing of the foregoing etching step, the etchedtop electrode 112′ and the etched MTJ (made of theetched layers 114′, 116′, and 118′) are formed and ahard mask 128 is deposited on top of thetop electrode 112′ and the photo-resist 130 is formed on top of thehard mask 128. In some embodiments, thehard mask 128 is made of oxide. - The photo-resist 124 serves as a mask during a further etching step that causes etching of the
hard mask 128. This additional etching step, in some embodiments and methods is done using dry etching techniques, in which thelayer 112 is etched with C12, or CF4, or CC13F, and layers 114, 116, and 118 are etched with CH3OH, or CO. The photo-resist 130 is removed during the step(s) ofFIG. 13 when etching is performed. -
FIG. 14 shows theelement 110, after the second etching step, where thelayers layers 118′, 116′, 114′, and 112′ with a width that is approximately that of thehard mask 128. - As earlier noted, in some embodiments and methods, the
layers 112′, 114′, and 118′ are etched in the additional etching step ofFIG. 14 with compounds containing fluoride (F), such as Carbon tetra fluoride (CF4) or Sulfa hexa fluoride (SF6), or Tri-Chloro-Fluoro-methane (also referred to as “Freon (CC13F)”). In some methods and embodiments, Ethel alcohol (C2H5OH) or CO with NH3 (Carbon mono-oxide with Amonia) is used to etch the free layer, the fixed layer and the barrier layer. - The etching process of the
layers 118′, 116′, 114′, and 112′ is advantageously stopped when the material manganese, in thelayer 120′ is detected. This advantageously prevents etching of thelayers 124′ and 122′ to avoid the risk of re-deposition of metal onto thelayer 116′, as experienced in prior art techniques. That is, copper from the layer 26 is not re-deposited onto the barrier layer nor is any metal from thelayers 124′ and 122′, which are both made of metal material. Thus, shorting between the fixed and free layers of the MTJ of theelement 110 is prevented. - Next, in
FIG. 15 , adielectric layer 132 is deposited on top of and around thelayers 118′, 116′, 114′, and 112′ and on top of and around thelayer 120. In some embodiments, thelayer 132 is made of silicon nitride (Si3N4). Most any dielectric material, such as silicon nitride, or deposited silicon dioxide or carbon-doped silicon dioxide (SiO2), can form thelayer 132. The purpose of this layer is primarily is to form a flat surface on top of the wafer. - The
layer 132 has a dome-type shape in that it is higher in areas that are directly on top of thelayers 112′-118′. This is due to the difference in height of thelayers 112′ to 118′ relative to thelayers 126 to 120′. - Next, in
FIG. 16 , a chemical mechanical polishing (CMP) process is performed on the structure of theelement 110, shown inFIG. 15 , resulting in the structure of theelement 110, shown inFIG. 16 . CMP results in flattening the top or dome-type structure of theelement 110 and leaves a substantially uniform-sized top of this layer. After CMP, the etcheddielectric layer 132′ is formed from thelayer 132, having a width that is substantially the same size as that of the MTJ and the etchedtop electrode 112′. - Next, a third etching step is performed to scale back the width of the
layer 132 to be suitably over the top and around thelayers 112′-118′ and no more, as shown inFIG. 16 to protect thelayer 116 from re-deposition during a further etching process. Thelayer 132, after etching is shown inFIG. 16 to form thelayer 132′. That is, the area of thelayer 132′ that is left on top and around these layers is sufficient to protect thelayer 116′ in further etching step(s), discussed below. - In
FIG. 17 , another masking process begins by forming another photo-resist 134 on top of thelayer 132′. The photo-resist 34 serves to protect thelayer 116′ when a third etching step is performed inFIG. 17 . In this process thelayer 132 is etched using C12, of CF4 or similar gases. Next, as discussed above, before alcohol or CO can be used to etch thelayers bottom electrode 124 can be etched by CF4, Ar, or similar gases. During this etching step, the photo-resist 134 is removed resulting in the structure of theelement 110 being that shown inFIG. 18 . The protection of thelayer 116′ by using the size of thelayer 132′ that is sufficient to protect the edges of thelayer 116′ from possible re-deposition of metal and therefore shorting, ensures reliability of theelement 110. - In some embodiments, the
bottom electrode 124 is made of heavy materials, such as tantalum (Ta) and tantalum nitride (TaN), or titanium nitride (TiN), or combination thereof - Although the present invention has been described in terms of specific embodiments, it is anticipated that alterations and modifications thereof will no doubt become apparent to those skilled in the art. It is therefore intended that the following claims be interpreted as covering all such alterations and modification as fall within the true spirit and scope of the invention.
Claims (17)