WO2001078116A2 - System for the preferential removal of silicon oxide - Google Patents
System for the preferential removal of silicon oxide Download PDFInfo
- Publication number
- WO2001078116A2 WO2001078116A2 PCT/US2001/011604 US0111604W WO0178116A2 WO 2001078116 A2 WO2001078116 A2 WO 2001078116A2 US 0111604 W US0111604 W US 0111604W WO 0178116 A2 WO0178116 A2 WO 0178116A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polishing
- abrasive
- fluoride ions
- substrate
- amine
- Prior art date
Abstract
Description
Claims